Copper-based dispersion hardened materials obtained by extrusion
Journal Article
·
· Powder Metallurgy and Metal Ceramics
OSTI ID:114823
- and others
Using the results of differential thermal analysis, the sintering parameters and extrusion temperatures for the fabrication of Cu-Cr-Zn-TiC powder alloys were determined. The optimal compositions, and techniques for their production were identified. Industrial tests of electrodes prepared by extrusion of the dispersion hardened materials showed that their durability is 3-5 times greater than that of standard electrodes.
- OSTI ID:
- 114823
- Journal Information:
- Powder Metallurgy and Metal Ceramics, Vol. 33, Issue 1-2; Other Information: PBD: Jul 1994; TN: Translated from Poroshkovaya Metallurgiya; Nos. 1-2, 43-46(Jan-Feb 1994)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Properties of dispersion hardening powdered copper alloys
RESEARCH STUDY FOR DEVELOPMENT OF ALUMINUM BASE ALLOYS BY POWDER METALLURGY TECHNIQUES. Interim Project Report for the Contract Period March 1, 1959 through February 29, 1960
Equal Channel Angular Extrusion Progress Report for March 1998 - May 1999
Journal Article
·
Fri Jul 01 00:00:00 EDT 1988
· Sov. Powder Metall. Met. Ceram. (Engl. Transl.); (United States)
·
OSTI ID:114823
RESEARCH STUDY FOR DEVELOPMENT OF ALUMINUM BASE ALLOYS BY POWDER METALLURGY TECHNIQUES. Interim Project Report for the Contract Period March 1, 1959 through February 29, 1960
Technical Report
·
Fri Aug 12 00:00:00 EDT 1960
·
OSTI ID:114823
Equal Channel Angular Extrusion Progress Report for March 1998 - May 1999
Technical Report
·
Fri Oct 01 00:00:00 EDT 1999
·
OSTI ID:114823
+5 more