STRAIN CORRELATIONS IN ALLOY 690 MATERIALS USING ELECTRON BACKSCATTER DIFFRACTION AND VICKERS HARDNESS
High chromium, nickel-base Alloy 690 exhibits an increased resistance to stress corrosion cracking (SCC) in pressurized water reactor (PWR) primary water environments over lower chromium alloy 600. As a result, Alloy 690 has been used to replace Alloy 600 for steam generator tubing, reactor pressure vessel nozzles and other pressure boundary components. However, recent laboratory crack-growth testing has revealed that heavily cold-worked Alloy 690 materials can become susceptible to SCC. To evaluate reasons for this increased SCC susceptibility, detailed characterizations have been performed on as-received and cold-worked Alloy 690 materials using electron backscatter diffraction (EBSD) and Vickers hardness measurements. Examinations were performed on cross sections of compact tension specimens that were used for SCC crack growth rate testing in simulated PWR primary water. Hardness and the EBSD integrated misorientation density could both be related to the degree of cold work for materials of similar grain size. However, a microstructural dependence was observed for strain correlations using EBSD and hardness which should be considered if this technique is to be used for gaining insight on SCC growth rates
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1140105
- Report Number(s):
- PNNL-SA-99738; 401001060
- Resource Relation:
- Conference: Corrosion 2014, March 9-13, 2014, San Antonio, Texas, Paper No. NACE-2014-4453
- Country of Publication:
- United States
- Language:
- English
Similar Records
The stress corrosion cracking behavior of alloys 690 and 152 WELD in a PWR environment.
ALLOY 690 SURFACE NANOSTRUCTURES DURING EXPOSURE TO PWR PRIMARY WATER AND POTENTIAL INFLUENCE ON STRESS CORROSION CRACKING INITIATION