Phase Stability and Mechanical Properties of Nuclear Grade FeCrAl Under LWR-Relevant Neutron Irradiation
Conference
·
OSTI ID:1134647
- ORNL
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). High Flux Isotope Reactor (HFIR)
- Sponsoring Organization:
- USDOE Office of Nuclear Energy (NE)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1134647
- Resource Relation:
- Conference: Nuclear Fuels & Structural Materials for Next Generation Nuclear Reactors, Reno, NV, USA, 20140615, 20140619
- Country of Publication:
- United States
- Language:
- English
Similar Records
ASSESSMENT OF DEFORMATION MECHANISMS IN NEUTRON-IRRADIATED ACCIDENT-TOLERANT FeCrAl ALLOYS VIA IN SITU MECHANICAL TESTING AND TEM ANALYSIS
Mechanical failure of fresh nuclear grade iron–chromium–aluminum (FeCrAl) cladding under simulated hot zero power reactivity initiated accident conditions
Mechanical properties of SiC composites neutron irradiated under light water reactor relevant temperature and dose conditions
Conference
·
Thu Aug 01 00:00:00 EDT 2019
·
OSTI ID:1134647
Mechanical failure of fresh nuclear grade iron–chromium–aluminum (FeCrAl) cladding under simulated hot zero power reactivity initiated accident conditions
Journal Article
·
Thu Jul 02 00:00:00 EDT 2020
· Journal of Nuclear Materials
·
OSTI ID:1134647
+2 more
Mechanical properties of SiC composites neutron irradiated under light water reactor relevant temperature and dose conditions
Journal Article
·
Tue Jul 04 00:00:00 EDT 2017
· Journal of Nuclear Materials
·
OSTI ID:1134647