IC W13_fephases Highlight:Solid-Solid Phase Boundary in Fe
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
- KTH Royal Inst. of Technology, Stockholm (Sweden)
Temperature of the fcc-bcc (face-centered cubic – body-centered cubic) solid-solid phase transition in Fe calculated as Teq = Tinst ΔEfcc-bcc/ΔEbcc-m. (where m. stands for martensitic mixture that bcc-Fe converts into at Tinst) maps out a curve which is consistent with the line of the fast recrystallization threshold observed in the recent experiments on Fe at ESRF.
- Research Organization:
- Los Alamos National Laboratory (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE National Nuclear Security Administration (NNSA)
- DOE Contract Number:
- AC52-06NA25396
- OSTI ID:
- 1127487
- Report Number(s):
- LA-UR-14-22512
- Country of Publication:
- United States
- Language:
- English
Similar Records
Thermodynamic analysis and evaluation of the Fe-Cr-Mn-N system
Decomposition of Fe-Ni martensite: Implications for the low-temperature ([<=]500 C) Fe-Ni phase diagram
High-Throughput Combinatorial Development of High-Entropy Alloys For Light-Weight Structural Applications
Journal Article
·
Mon Nov 01 00:00:00 EST 1993
· Metallurgical Transactions, A (Physical Metallurgy and Materials Science); (United States)
·
OSTI ID:1127487
Decomposition of Fe-Ni martensite: Implications for the low-temperature ([<=]500 C) Fe-Ni phase diagram
Journal Article
·
Mon Aug 01 00:00:00 EDT 1994
· Metallurgical Transactions, A (Physical Metallurgy and Materials Science); (United States)
·
OSTI ID:1127487
High-Throughput Combinatorial Development of High-Entropy Alloys For Light-Weight Structural Applications
Technical Report
·
Fri Dec 29 00:00:00 EST 2017
·
OSTI ID:1127487
+2 more