Title: Atomic structure of interphase boundary enclosing bcc precipitate formed in fcc matrix in a Ni-Cr alloy

Journal Article · · Metallurgical Transactions, A
DOI:https://doi.org/10.1007/BF02670668· OSTI ID:109777

The atomic structure of the interphase boundary enclosing body-centered cubic (bcc) lath-shape precipitates formed in the face-centered cubic (fcc) matrix of a Ni-45 mass pct Cr alloy was examined by means of conventional and high-resolution transmission electron microscopy (HRTEM). Growth ledges were observed on the broad faces of the laths. The growth ledge terrace (with the macroscopic habit plane {approximately}(112){sub fcc}//(23{bar 1}){sub bcc}) contains a regular array of structural ledges whose terrace is formed by the (111){sub fcc}//(110){sub bcc} planes. A structural ledge has an effective Burgers vector corresponding to an a/12[1{bar 2}1]{sub fcc} transformation dislocation in the fcc {yields} bcc transformation. The side facet (and presumably the growth ledge riser) of the bcc lath contains two distinct types of lattice dislocation accommodating transformation strains. One type is glissile dislocations, which exist on every six layers of parallel close-packed planes. These perfectly accommodate the shear strain caused by the stacking sequence change from fcc to bcc. The second set is sessile misfit dislocations ({approximately}10 nm apart) whose Burgers vector is a/3[111]{sub fcc} = a/2[110]{sub bcc}. These perfectly accommodate the dilatational strain along the direction normal to the parallel close-packed planes. These results demonstrate that the interphase boundaries enclosing the laths are all semicoherent. Nucleation and migration of growth ledges, which are controlled by diffusion of substitutional solute atoms, result in the virtual displacement of transformation dislocations accompanying the climb of sessile misfit dislocations and the glide of glissile dislocations simultaneously. Such a growth mode assures the retention of atomic site correspondence across the growing interface.

OSTI ID:
109777
Journal Information:
Metallurgical Transactions, A, Vol. 26, Issue 8; Other Information: PBD: Aug 1995
Country of Publication:
United States
Language:
English

Similar Records

Interface structure of faceted lath-shaped Cr precipitates in a Cu-0.33 wt% Cr alloy
Journal Article · Mon Mar 23 00:00:00 EST 1998 · Acta Materialia · OSTI ID:109777

The invariant line and precipitate morphology in fcc-bcc systems
Journal Article · Thu Sep 01 00:00:00 EDT 1994 · Metallurgical Transactions, A (Physical Metallurgy and Materials Science); (United States) · OSTI ID:109777

The role of structural ledges at phase boundaries; 3: F. c. c. -b. c. c. interfaces in Kurdjumov-Sachs orientation
Journal Article · Fri Apr 01 00:00:00 EST 1994 · Acta Metallurgica et Materialia; (United States) · OSTI ID:109777