The influences of temperature and microstructure on the tensile properties of a CoCrFeMnNi high-entropy alloy
- ORNL
- Institute of Physics of Materials, Brno, Czech Republic
- Ruhr University, Bochum, Germany
An equiatomic CoCrFeMnNi high-entropy alloy, which crystallizes in the face-centered cubic (FCC) crystal structure, was produced by arc melting and drop casting. The drop-cast ingots were homogenized, cold rolled, and recrystallized to obtain single-phase microstructures with three different grain sizes in the range 4~160 m. Quasi-static tensile tests were then performed at temperatures between 77 and 1073 K. Yield strength, ultimate tensile strength and ductility all increased with decreasing temperature. During the initial stages of plasticity (up to ~2% strain), deformation occurs by planar dislocation glide on the normal FCC slip system {111} 110 at all temperatures and grain sizes investigated. Undissociated 1/2 110 dislocations were observed, as were numerous stacking faults, which imply the dissociation of several of these dislocations into 1/6 112 Shockley partials. At later stages ( 20% strain), nanoscale deformation twins were observed after interrupted tests at 77 K, but not in specimens tested at room temperature where plasticity occurred exclusively by dislocations which organized into cells. Deformation twinning, by continually decreasing the mean free path of dislocations during tensile testing, produces a high degree of work hardening and a significant increase in the ultimate tensile strength. This increased work hardening prevents the early onset of necking instability and is a reason for the enhanced ductility observed at 77 K. A second way in which twinning can contribute to ductility is by providing an additional deformation mode to accommodate plasticity. However, it cannot explain the increase in yield strength with decreasing temperature in our high-entropy alloy since twinning was not observed in the early stages of plastic deformation. Since strong temperature dependencies of yield strength are also seen in binary FCC solid solution alloys, it may be an inherent solute effect, which needs further study.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1089775
- Journal Information:
- Acta Materialia, Vol. 61, Issue 15; ISSN 1359-6454
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructures and mechanical properties of compositionally complex Co-free FeNiMnCr18 FCC solid solution alloy
Effect of Strain Rate on the Tensile Behavior of CoCrFeNi and CoCrFeMnNi High-Entropy Alloys