Economical Route to Produce High Seebeck Coefficient Calcium Cobaltate for Bulk Thermoelectric Applications
Journal Article
·
· Journal of the American Ceramic Society
- Lamar University
- ORNL
Phase pure calcium cobaltate (Ca1.24Co1.62O3.86) was prepared by Self-propagating High-temperature Synthesis (SHS) followed by a short post heat treatment. Prepared powders were characterized by XRD for phase purity, and SEM for particle size and distribution. Temperature histories at the center and on the surface of reaction pellet during the SHS process were monitored and recorded. Particles size of synthesized powders was reduced using a planetary mill to increase its specific surface area. Electrical conductivity, thermal conductivity and Seebeck coefficient of the prepared power were measured and figure of merit was reported.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). High Temperature Materials Lab. (HTML)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1045843
- Journal Information:
- Journal of the American Ceramic Society, Vol. 94, Issue 10; ISSN 0002-7820
- Country of Publication:
- United States
- Language:
- English
Similar Records
Thermoelectric properties of Fe-Si alloys - effects of oxidation and SiO{sub 2} dispersion
Anisotropy analysis of thermoelectric properties of Bi{sub 2}Te{sub 2.9}Se{sub 0.1} prepared by SPS method
Physical and electrochemical study of cobalt oxide nano- and microparticles
Conference
·
Tue Dec 31 00:00:00 EST 1996
·
OSTI ID:1045843
Anisotropy analysis of thermoelectric properties of Bi{sub 2}Te{sub 2.9}Se{sub 0.1} prepared by SPS method
Journal Article
·
Tue Jun 26 00:00:00 EDT 2012
· AIP Conference Proceedings
·
OSTI ID:1045843
Physical and electrochemical study of cobalt oxide nano- and microparticles
Journal Article
·
Tue Jul 01 00:00:00 EDT 2014
· Materials Characterization
·
OSTI ID:1045843
+3 more