One suggested strategy for improving the performance of thermal barrier coating (TBC) systems used to protect hot section components in gas turbines is the addition of low levels of dopants to the Ni-base superalloy substrate. To quantify the benefit of these dopants, the oxidation behavior of three commercial superalloys with different Y and La contents was evaluated with and without a NiCoCrAlYHfSi bond coating deposited by high velocity oxygen fuel (HVOF) spraying. Cyclic oxidation experiments were conducted in dry O{sub 2} at 1050, 1100 and 1150 C. At the highest temperature, the bare superalloy without La showed more attack due to its lower Al content but no difference in oxidation rate or scale adhesion was noted at lower temperatures. With a bond coating, the alumina scale was non-uniform in thickness and spalled at each temperature. Among the three coated superalloys, no clear difference in oxide growth rate or scale adhesion was observed. Evaluations with a YSZ top coat and a bond coating without Hf are needed to better determine the effect of superalloy dopants on high temperature oxidation performance.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- FE USDOE - Office of Fossil Energy (FE)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1030615
- Resource Relation:
- Conference: ICMCTF, San Diego, CA, USA, 20110502, 20110506
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of higher water vapor content on TBC performance
Effect of Water Vapor on the 1100oC Oxidation Behavior of Plasma-Sprayed TBCs with HVOF NiCoCrAlX Bond Coatings