Postirradiation analysis of the latest high uranium density miniplate test: RERTR 8.
- Nuclear Engineering Division
Results of destructive examination of fuel miniplates irradiated in the RERTR-8 test are discussed. Metallographic features of dispersion fuel containing fuel particles of U-7wt%Mo with 1wt% Ti or 2wt% Zr are analyzed. It is hypothesized that Zr, either as alloy addition or fission product, may have a destabilizing effect on fission gas behavior. The purpose of miniplate test RERTR-8 was to obtain irradiation performance data on monolithic fuel plates fabricated by friction bonding (FB) and isostatic hot pressing (HIP), as well as dispersion fuel plates that contain U-7Mo fuel particles alloyed with small amounts of Zr or Ti (see Fig. 1). The results of the monolithic plates destructively examined to date were presented at the 2007 RERTR meeting in Prague. This paper presents the first results on the dispersion plates with Ti and Zr additions to U-7Mo. The effect of Ti and Zr additions to U-7wt%Mo on the extent of fuel-aluminum interdiffusion, although measureable, is small in absolute terms because of the overwhelming effect of the 5% Si addition to the Al matrix. Ti additions to the U-7wt%Mo have no discernable effect on swelling behavior of the fuel. However, there are indications that the addition of Zr may have a destabilizing effect on fission gas behavior at high burnup.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE National Nuclear Security Administration (NNSA)
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 1013973
- Report Number(s):
- ANL/NE/CP-60993; TRN: US1102576
- Resource Relation:
- Conference: RRFM 2008; Mar. 2, 2008 - Mar. 5, 2008; Hamburg, Germany
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Progress on RERTR activities in Argentina
Microstructural characterization of an irradiated RERTR-6 U-7Mo/AA4043 alloy dispersion fuel plate specimen blister-tested to a final temperature of 500°C