Depletion Interactions: Effects of Added Homopolymer on Ordered Phases Formed by Spherical Block Copolymer Micelles
- UMM
Three distinct poly(styrene-b-isoprene) (SI) diblock copolymers with molecular weights of 16-16, 38-14, and 50-13 kDa for styrene and isoprene, respectively, formed spherical micelles when dissolved in diethyl phthalate (DEP). Since DEP is a styrene-selective solvent, micelles with polyisoprene in the core and polystyrene in the corona were formed. At block copolymer concentrations of 20%, 16%, and 14% in DEP, the spherical micelles of SI(16-16), SI(38-14), and SI(50-13) pack onto a face-centered cubic (FCC) lattice, a mixture of FCC and body-centered cubic (BCC) lattices, and a BCC lattice, respectively. Polystyrene homopolymers with molecular weights of 4, 48, and 180 kDa were added to these ordered solutions. The following general trends were observed: the FCC phase tended to disorder, and samples that originally behaved like soft solids exhibited liquidlike flow behavior. The effect increased strongly with both the molecular weight and concentration of homopolymer in the solution. Furthermore, the BCC lattice tended to be displaced by the FCC lattice, or to disorder, when homopolymer was added. These results can be explained by invoking depletion interactions, which have been studied extensively in colloid/polymer mixtures. However, the phenomenon differs in certain details from colloidal systems because the addition of homopolymer can also influence the aggregation number of the micelles, which in turn affects the lattice packing of the micelles.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States). Advanced Photon Source (APS)
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 1006987
- Journal Information:
- Macromolecules, Vol. 41, Issue (22) ; 2008
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Cornucopia of Nanoscale Ordered Phases in Sphere-Forming Tetrablock Terpolymers
Effect of monomer sequencing on the phase behavior of novel block copolymer/homopolymer blends