Effects of Ion Beam on Nanoindentation Characteristics of Glassy Polymeric Carbon Surface
- FFCLRP-USP, Ribeirao Preto, SP, Brazil
- UNESP, Guaratingueta, SP, Brazil
- Alabama A&M University, Normal
- ORNL
Glassy polymeric carbon (GPC) is a useful material for medical applications due to its chemical inertness and biocompatible characteristics. Mitral and aortic and hydrocephalic valves are examples of GPC prosthetic devices that have been fabricated and commercialized in Brazil. In this work, ion beam was used to improve the mechanical characteristics of GPC surface and therefore to avoid the propagation of microcracks where the cardiac valves are more fragile. A control group of phenolic resin samples heat-treated at 300, 400, 700, 1000, 1500, and 2500 C was characterized by measuring their hardness and Young's reduced elastic modulus with the depth of indentation. The control group was compared to results obtained with samples heat-treated at 700, 1000, and 1500 C and bombarded with energetic ions of silicon, carbon, oxygen, and gold at energies of 5, 6, 8, and 10 MeV, respectively, with fluences between 1.0 x 10{sup 13} and 1.0 x 10{sup 16} ions/cm{sup 2}. GPC nonbombarded samples showed that hardness depends on the heat treatment temperature (HTT), with a maximum hardness for heat treatment at 1000 C. The comparison between the control group and bombarded group also showed that hardness, after bombardment, had a greater increase for samples prepared at 700 C than for samples prepared at higher temperatures. The Young's elastic modulus presents an exponential relationship with depth. The parameters obtained by fitting depend on the HTT and on the ion used in the bombardment more than on energy and fluence. The hardness results show clearly that bombardment can promote carbonization, increase the linkage between the chains of the polymeric material, and promote recombination of broken bonds in lateral groups that are more numerous for samples heat-treated at 700 C.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1003382
- Journal Information:
- Surface and Coatings Technology, Vol. 196, Issue 1-3; ISSN 0257-8972
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structural Modifications And Mechanical Degradation Of Ion Irradiated Glassy Polymer Carbon
Surface treatment of Glassy Polymeric Carbon artifacts for medical applications