Surface chemistry and bonding configuration of ultrananocrystalline diamond surfaces and their effects on nanotribological properties.
We present a comprehensive study of surface composition and nanotribology for ultrananocrystalline diamond (UNCD) surfaces, including the influence of film nucleation on these properties. We describe a methodology to characterize the underside of the films as revealed by sacrificial etching of the underlying substrate. This enables the study of the morphology and composition resulting from the nucleation and initial growth of the films, as well as the characterization of nanotribological properties which are relevant for applications including micro-/nanoelectromechanical systems. We study the surface chemistry, bonding configuration, and nanotribological properties of both the topside and the underside of the film with synchrotron-based x-ray absorption near-edge structure spectroscopy to identify the bonding state of the carbon atoms, x-ray photoelectron spectroscopy to determine the surface chemical composition, Auger electron spectroscopy to further verify the composition and bonding configuration, and quantitative atomic force microscopy to study the nanoscale topography and nanotribological properties. The films were grown on SiO{sub 2} after mechanically polishing the surface with detonation synthesized nanodiamond powder, followed by ultrasonication in a methanol solution containing additional nanodiamond powder. The sp{sup 2} fraction, morphology, and chemistry of the as-etched underside are distinct from the topside, exhibiting a higher sp{sup 2} fraction, some oxidized carbon, and a smoother morphology. The nanoscale single-asperity work of adhesion between a diamond nanotip and the as-etched UNCD underside is far lower than for a silicon-silicon interface (59.2 {+-} 2 vs 826 {+-} 186 mJ/m{sup 2}, respectively). Exposure to atomic hydrogen dramatically reduces nanoscale adhesion to 10.2 {+-} 0.4 mJ/m{sup 2}, at the level of van der Waals interactions and consistent with recent ab initio calculations. Friction is substantially reduced as well, demonstrating a direct link between the surface chemistry and nanoscale friction. The proposed mechanism, supported by the detailed surface spectroscopic analysis, is the elimination of reactive (e.g., C*-), polar (e.g., C-O), and {pi}-bonded (C-C) surface groups, which are replaced by fully saturated, hydrogen-terminated surface bonds to produce an inert surface that interacts minimally with the contacting counterface.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC); US Air Force Office of Scientific Research (AFOSR)
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 1000687
- Report Number(s):
- ANL/MSD/JA-68696; TRN: US201101%%468
- Journal Information:
- Phys. Rev. B, Vol. 76, Issue Dec. 2007
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Morophology and electronic straucture in nitrogen-doped ultrananocrystalline diamond.
Near-Edge X-ray Absorption Fine Structure Imaging of Spherical and Flat Counterfaces of Ultrananocrystalline Diamond Tribological Contacts: A Correlation of Surface Chemistry and Friction