Title: Analysis of irradiated U-7wt%Mo dispersion fuel microstructures using automated image processing

The High Performance Research Reactor Fuel Development (HPPRFD) program is responsible for developing low enriched uranium (LEU) fuel substitutes for high performance reactors fueled with highly enriched uranium (HEU) that have not yet been converted to LEU. The uranium-molybdenum (U-Mo) fuel system was selected for this effort. In this study, fission gas pore segmentation was performed on U-7wt%Mo dispersion fuel samples at three separate fission densities using an automated image processing interface developed in MATLAB. Pore size distributions were attained that showed both expected and unexpected fission gas behavior. In general, it proved challenging to identify any dominant trends when comparing fission bubble data across samples from different fuel plates due to varying compositions and fabrication techniques. Here, the results exhibited fair agreement with the fission density vs. porosity correlation developed by the Russian reactor conversion program.
Authors:
 [1] ;  [1] ;  [2] ;  [3] ;  [3] ;  [3] ;  [3]
  1. Colorado School of Mines, Golden, CO (United States)
  2. Oregon State Univ., Corvallis, OR (United States)
  3. Idaho National Lab. (INL), Idaho Falls, ID (United States)
Publication Date:
OSTI Identifier:
1294498
Report Number(s):
INL/JOU--15-35414
Journal ID: ISSN 0022-3115; PII: S0022311516301015
Grant/Contract Number:
AC07-05ID14517
Type:
Accepted Manuscript
Journal Name:
Journal of Nuclear Materials
Additional Journal Information:
Journal Volume: 475; Journal Issue: C; Journal ID: ISSN 0022-3115
Publisher:
Elsevier
Research Org:
Idaho National Laboratory, Idaho Falls, ID (United States)
Sponsoring Org:
USDOE
Country of Publication:
United States
Language:
English
Subject:
11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS; 36 MATERIALS SCIENCE; 97 MATHEMATICS AND COMPUTING nuclear fuel; MATLAB; automated image analysis; fission bubbles; fission density; porosity