Title: Effect of tip radius on the incipient plasticity of chromium studied by nanoindentation

The onset of plasticity in Cr was investigated by nanoindentation using indenters with tip radii ranging from 60 to 759 nm. The stress for incipient plasticity was found to increase with decreasing tip radius. We find that the cumulative pop-in probability on load could be described successfully by a combined model over the full range of tip radius, indicating that the incipient plasticity might be triggered either by the homogeneous nucleation of dislocation or by the activation of existing dislocations underneath the indenter.
Authors:
 [1] ;  [2] ;  [1]
  1. Univ. of Tennessee, Knoxville, TN (United States). Dept. of Materials Science and Engineering
  2. Univ. of Tennessee, Knoxville, TN (United States). Dept. of Materials Science and Engineering; Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Materials Science & Technology Division
Publication Date:
OSTI Identifier:
1286763
Grant/Contract Number:
AC05-00OR22725; DMR-0905979
Type:
Accepted Manuscript
Journal Name:
Scripta Materialia
Additional Journal Information:
Journal Volume: 94; Journal Issue: C; Journal ID: ISSN 1359-6462
Publisher:
Elsevier
Research Org:
Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
Sponsoring Org:
USDOE Office of Science (SC), Basic Energy Sciences (BES) (SC-22); National Science Foundation (NSF)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE Nanoindentation; Onset of yielding; Dislocation dynamics; Tip radius effect; Metallic material