Nitriding of a high entropy FeNiMnAlCr alloy

Meng, Fanling; Baker, Ian

doi:10.1016/j.jallcom.2015.05.021

Title: Nitriding of a high entropy FeNiMnAlCr alloy

Full Record
Other Related Research

Authors:: Meng, Fanling; Baker, Ian

Publication Date:: Thu Oct 01 00:00:00 EDT 2015

Sponsoring Org.:: USDOE

OSTI Identifier:: 1254364

Resource Type:: Publisher's Accepted Manuscript

Journal Name:: Journal of Alloys and Compounds

Additional Journal Information:: Journal Name: Journal of Alloys and Compounds Journal Volume: 645 Journal Issue: C; Journal ID: ISSN 0925-8388

Publisher:: Elsevier

Country of Publication:: Netherlands

Language:: English

Citation Formats


                    Meng, Fanling, and Baker, Ian. Nitriding of a high entropy FeNiMnAlCr alloy.  Netherlands: N. p., 2015. 
Web.  doi:10.1016/j.jallcom.2015.05.021.

Copy to clipboard


                    Meng, Fanling, & Baker, Ian. Nitriding of a high entropy FeNiMnAlCr alloy.  Netherlands.  https://doi.org/10.1016/j.jallcom.2015.05.021

Copy to clipboard


                    Meng, Fanling, and Baker, Ian. Thu .  
"Nitriding of a high entropy FeNiMnAlCr alloy".  Netherlands.  https://doi.org/10.1016/j.jallcom.2015.05.021.

Copy to clipboard


                    
@article{osti_1254364,

  title        = {Nitriding of a high entropy FeNiMnAlCr alloy},

  author       = {Meng, Fanling and Baker, Ian},

  abstractNote = {},

  doi          = {10.1016/j.jallcom.2015.05.021},

  journal      = {Journal of Alloys and Compounds},

  number       = C,

  volume       = 645,

  place        = {Netherlands},

  year         = {Thu Oct 01 00:00:00 EDT 2015},

  month        = {Thu Oct 01 00:00:00 EDT 2015}

}

Copy to clipboard

Journal Article:

Free Publicly Available Full Text

Accepted Manuscript (Publisher)

Publisher's Version of Record
https://doi.org/10.1016/j.jallcom.2015.05.021

Other availability

Search WorldCat to find libraries that may hold this journal

Citation Metrics:

Cited by: 46 works

Citation information provided by
Web of Science

Save / Share:

Export Metadata

Save to My Library

Similar Records in DOE PAGES and OSTI.GOV collections:

Interstitial strengthening of a f.c.c. FeNiMnAlCr high entropy alloy

Journal Article Wang, Zhangwei ; Baker, Ian - Materials Letters

Not provided.
https://doi.org/10.1016/j.matlet.2016.05.122
Interstitial strengthening of a f.c.c. FeNiMnAlCr high entropy alloy

Journal Article Wang, Zhangwei ; Baker, Ian - Materials Letters
Cited by 91
https://doi.org/10.1016/j.matlet.2016.05.122
Microband induced plasticity and the temperature dependence of the mechanical properties of a carbon-doped FeNiMnAlCr high entropy alloy

Journal Article Wang, Zhangwei ; Bei, Hongbin ; Baker, Ian - Materials Characterization

Here, the uniaxial mechanical properties of the high entropy alloy (HEA) Fe_40.4Ni_11.3Mn_34.8Al_7.5Cr₆ doped with 1.1 at.% C have been determined for both the as-cast and recrystallized states at temperatures from 77 to 973 K. Very high yield strengths were obtained at 77 K of 928 MPa for the as-cast HEA and 1037 MPa for the recrystallized HEA. The yield strength decreased sharply to 293 K and more slowly to 973 K, where it was ~200 MPa [11] in both conditions. The lattice friction stress, which results from the increase of the Peierls barrier, was the major contributor to the largemore »« less
Cited by 33
https://doi.org/10.1016/j.matchar.2018.03.017

Full Text Available
Microband induced plasticity and the temperature dependence of the mechanical properties of a carbon-doped FeNiMnAlCr high entropy alloy

Journal Article Wang, Zhangwei ; Bei, Hongbin ; Baker, Ian - Materials Characterization

Highlights: • A superior fcc HEA with the strength of 1.5 GPa at the cryogenic condition is developed. • The strengthening mechanisms of HEAs at different temperatures are clarified. • The temperature dependence of MBIP effect is revealed. - Abstract: The uniaxial mechanical properties of the high entropy alloy (HEA) Fe{sub 40.4}Ni{sub 11.3}Mn{sub 34.8}Al{sub 7.5}Cr{sub 6} doped with 1.1 at.% C have been determined for both the as-cast and recrystallized states at temperatures from 77 to 973 K. Very high yield strengths were obtained at 77 K of 928 MPa for the as-cast HEA and 1037 MPa for the recrystallizedmore »« less
https://doi.org/10.1016/J.MATCHAR.2018.03.017
Enhanced mechanical properties of carbon-doped FeNiMnAlCr high entropy alloy via hot-rolling

Journal Article Wu, Margaret ; Yang, Chao ; Kuijer, Michael ; ... - Materials Characterization

This work demonstrates an improvement in the mechanical performance of the high entropy alloy Fe_40.4Ni_11.3Mn_34.8Al_7.5Cr₆ containing 1.1 at. % carbon (CHEA) by hot-rolling followed by annealing at 1323 K. The microstructure was examined using scanning electron microscopy, electron backscatter diffraction, X-ray diffraction, and transmission electron microscopy. Room-temperature tensile tests were used to assess the alloy's mechanical properties. The presence of dense dislocation walls indicate that the alloy has not fully recrystallized and, moreover, the deformation substructure and the large fraction of Σ3 twin boundaries contribute to the high room temperature yield strength (~523 MPa). Despite the presence of substantial dislocationmore »« less
Cited by 4
https://doi.org/10.1016/j.matchar.2019.109983

Full Text Available

Similar Records