Title: High performance carbon fibers from very high molecular weight polyacrylonitrile precursors

In this study, carbon fibers are unique reinforcing agents for lightweight composite materials due to their outstanding mechanical properties and low density. Current technologies are capable of producing carbon fibers with 90-95% of the modulus of perfect graphite (~1025 GPa). However, these same carbon fibers possess less than 10% of the theoretical carbon fiber strength, estimated to be about 100 GPa.[1] Indeed, attempts to increase carbon fiber rigidity results in lower breaking strength. To develop advanced carbon fibers with both very high strength and modulus demands a new manufacturing methodology. Here, we report a method of manufacturing high strength, very high modulus carbon fibers from a very high molecular weight (VHMW) polyacrylonitrile (PAN) precursor without the use of nanomaterial additives such as nucleating or structure-templating agents, as have been used by others.[2,3]
Authors:
 [1] ;  [1] ;  [2] ;  [2] ;  [2] ;  [2] ;  [2] ;  [2] ;  [2] ;  [3] ;  [2]
  1. Univ. of Kentucky, Lexington, KY (United States)
  2. Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
  3. Virginia Polytechnic Inst. and State Univ. (Virginia Tech), Blacksburg, VA (United States)
Publication Date:
OSTI Identifier:
1250406
Grant/Contract Number:
AC05-00OR22725
Type:
Accepted Manuscript
Journal Name:
Carbon
Additional Journal Information:
Journal Volume: 101; Journal Issue: C; Journal ID: ISSN 0008-6223
Publisher:
Elsevier
Research Org:
Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
Sponsoring Org:
USDOE
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE