Title: SANS Investigations of CO2 Adsorption in Microporous Carbon

The high pressure adsorption behavior of CO2 at T = 296 K in microporous carbon was investigated by small-angle neutron scattering (SANS) technique. A strong densification of CO2 in micropores accompanied by non-monotonic adsorption-induced pore deformation was observed. The density of confined CO2 increases rapidly with pressure and reaches the liquid –like density at 20 bar, which corresponds to the relative pressure of P/Psat ~0.3. At P > 20 bar density of confined CO2 increases slowly approaching a plateau at higher pressure. The size of micropores first increases with pressure, reaches a maximum at 20 bar, and then decreases with pressure. A complementary SANS experiment conducted on the same microporous carbon saturated with neutron-transparent and non-adsorbing inert gas argon shows no deformation of micropores at pressures up to ~200 bars. This result demonstrates that the observed deformation of micropores in CO2 is an adsorption-induced phenomenon, caused by the solvation pressure - induced strain and strong densification of confined CO2 .
Authors:
 [1] ;  [1] ;  [1] ;  [1] ;  [1] ;  [1]
  1. Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
Publication Date:
OSTI Identifier:
1214021
Grant/Contract Number:
AC05-00OR22725
Type:
Accepted Manuscript
Journal Name:
Carbon
Additional Journal Information:
Journal Volume: 95; Journal ID: ISSN 0008-6223
Publisher:
Elsevier
Research Org:
Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). High Flux Isotope Reactor (HFIR)
Sponsoring Org:
USDOE Office of Science (SC)
Country of Publication:
United States
Language:
English
Subject:
54 ENVIRONMENTAL SCIENCES