Title: Sessile dislocations by reactions in NiAl severely deformed at room temperature

B2 ordered NiAl is known for its poor room temperature (RT) ductility; failure occurs in a brittle like manner even in ductile single crystals deforming by single slip. In the present study NiAl was severely deformed at RT using the method of high pressure torsion (HPT) enabling the hitherto impossible investigation of multiple slip deformation. Methods of transmission electron microscopy were used to analyze the dislocations formed by the plastic deformation showing that as expected dislocations with Burgers vector a(100) carry the plasticity during HPT deformation at RT. In addition, we observe that they often form a(110) dislocations by dislocation reactions; the a(110) dislocations are considered to be sessile based on calculations found in the literature. It is therefore concluded that the frequently encountered 3D dislocation networks containing sessile a(110) dislocations are pinned and lead to deformation-induced embrittlement. In spite of the severe deformation, the chemical order remains unchanged.
Authors:
 [1] ;  [2] ;  [1] ;  [1]
  1. Univ. of Vienna (Austria). Faculty of Physics
  2. Univ. of Vienna (Austria). Faculty of Physics; Lawrence Berkeley National Lab. (LBNL), Berkeley, CA (United States)
Publication Date:
OSTI Identifier:
1208056
Grant/Contract Number:
AC02-05CH11231
Type:
Accepted Manuscript
Journal Name:
Journal of Alloys and Compounds
Additional Journal Information:
Journal Volume: 621; Journal Issue: C; Journal ID: ISSN 0925-8388
Publisher:
Elsevier
Research Org:
Lawrence Berkeley National Laboratory (LBNL), Berkeley, CA (United States)
Sponsoring Org:
USDOE
Country of Publication:
United States
Language:
English
Subject:
High pressure torsion; B2 intermetallic compound; Transmission electron microscopy; 3D dislocation networks; Deformation-induced embrittlement