Synthesis and thermoelectric properties of Ce(Ru0.67Rh0.33)4Sb12. Geoff D. Staneff1
 

Summary: Synthesis and thermoelectric properties of Ce(Ru0.67Rh0.33)4Sb12.
Geoff D. Staneff1
, Paul D. Asimow2
,. Thierry Caillat3
1
Department of Materials Science, California Institute of Technology
Pasadena, CA 91125
2
Division of Geological and Planetary Sciences, California Institute of Technology
Pasadena, CA 91125
3
Jet Propulsion Laboratory
Pasadena, CA 91109
Abstract
Exotic filled skutterudite compositions show promise for thermoelectric applications.
Current work was undertaken with a nominal composition of Ce(Ru0.67Rh0.33)4Sb12 to
experimentally verify its potential as an n-type thermoelectric material. Nominal
electroneutrality was expected at 0.89 cerium filling and fully filled materials were
expected to be strongly n-type. Filled precursors of the nominal composition were
synthesized using straightforward solid state reaction techniques, but standard synthesis

  

Source: Asimow, Paul D. - Division of Geological and Planetary Sciences, California Institute of Technology,

 