Evaluation of Neutron Irradiated Silicon Carbide and Silicon Carbide Composites
The effects of fast neutron irradiation on SiC and SiC composites have been studied. The materials used were chemical vapor deposition (CVD) SiC and SiC/SiC composites reinforced with either Hi-Nicalon{trademark} Type-S, Hi-Nicalon{trademark} or Sylramic{trademark} fibers fabricated by chemical vapor infiltration. Statistically significant numbers of flexural samples were irradiated up to 4.6 x 10{sup 25} n/m{sup 2} (E>0.1 MeV) at 300, 500 and 800 C in the High Flux Isotope Reactor at Oak Ridge National Laboratory. Dimensions and weights of the flexural bars were measured before and after the neutron irradiation. Mechanical properties were evaluated by four point flexural testing. Volume increase was seen for all bend bars following neutron irradiation. Magnitude of swelling depended on irradiation temperature and material, while it was nearly independent of irradiation fluence over the fluence range studied. Flexural strength of CVD SiC increased following irradiation depending on irradiation temperature. Over the temperature range studied, no significant degradation in mechanical properties was seen for composites fabricated with Hi-Nicalon{trademark} Type-S, while composites reinforced with Hi-Nicalon{trademark} or Sylramic fibers showed significant degradation. The effects of irradiation on the Weibull failure statistics are also presented suggesting a reduction in the Weibull modulus upon irradiation. The cause of this potential reduction is not known.
- Research Organization:
- Knolls Atomic Power Lab. (KAPL), Niskayuna, NY (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- DE-AC12-00SN39357
- OSTI ID:
- 903202
- Report Number(s):
- LM-07K017; JNUMAM; TRN: US200719%%640
- Journal Information:
- Journal of Nuclear Materials, Journal Name: Journal of Nuclear Materials; ISSN 0022-3115
- Country of Publication:
- United States
- Language:
- English
Similar Records
Stability of SiC and its Composites at High Neutron Fluence
Neutron-irradiation creep of silicon carbide materials beyond the initial transient