Synthesis, characterization and electrochemmistry of lithium battery electrodes : xLi{sub 2}MnO{sub 3}{center_dot}(1-x)LiMn{sub 0.333}Ni{sub 0.333}Co{sub 0.333}O{sub2} (0{le}x{le}0.7).
Lithium- and manganese-rich layered electrode materials, represented by the general formula xLi{sub 2}MnO{sub 3} {center_dot} (1-x)LiMO{sub 2} in which M is Mn, Ni, and Co, are of interest for both high-power and high-capacity lithium ion cells. In this paper, the synthesis, structural and electrochemical characterization of xLi{sub 2}MnO{sub 3} {center_dot} (1-x)LiMn{sub 0.333}Ni{sub 0.333}Co{sub 0.333}O{sub 2} electrodes over a wide compositional range (0 {le} x {le} 0.7) is explored. Changes that occur to the compositional, structural, and electrochemical properties of the electrodes as a function of x and the importance of using a relatively high manganese content and a high charging potential (>4.4 V) to generate high capacity (>200 mAh/g) electrodes are highlighted. Particular attention is given to the electrode composition 0.3Li{sub 2}MnO{sub 3} {center_dot} 0.7LiMn{sub 0.333}Ni{sub 0.333}Co{sub 0.333}O{sub 2} (x = 0.3) which, if completely delithiated during charge, yields Mn{sub 0.533}Ni{sub 0.233}Co{sub 0.233}O{sub 2}, in which the manganese ions are tetravalent and, when fully discharged, LiMn{sub 0.533}Ni{sub 0.233}Co{sub 0.233}O{sub 2}, in which the average manganese oxidation state (3.44) is marginally below that expected for a potentially damaging Jahn-Teller distortion (3.5). Acid treatment of 0.3Li{sub 2}MnO{sub 3} {center_dot} 0.7LiMn{sub 0.333}Ni{sub 0.333}Co{sub 0.333}O{sub 2} composite electrode structures with 0.1 M HNO{sub 3} chemically activates the Li{sub 2}MnO{sub 3} component and essentially eliminates the first cycle capacity loss but damages electrochemical behavior, consistent with earlier reports for Li{sub 2}MnO{sub 3}-stabilized electrodes. Differences between electrochemical and chemical activation of the Li{sub 2}MnO{sub 3} component are discussed. Electrochemical charge/discharge profiles and cyclic voltammogram data suggest that small spinel-like regions, generated in cycled manganese-rich electrodes, serve to stabilize the electrodes, particularly at low lithium loadings (high potentials). The study emphasizes that, for high values of x, a relatively small LiMO{sub 2} concentration stabilizes a layered Li{sub 2}MnO{sub 3} electrode to reversible lithium insertion and extraction when charged to a high potential.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- EE
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 985118
- Report Number(s):
- ANL/CSE/JA-62274; ISSN 1520-5002; TRN: US1006079
- Journal Information:
- Chem. Mater., Vol. 20, Issue 19 ; 2008; ISSN 0897-4756
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Stabilization xLi{sub 2}MnO{sub 3}{sm_bullet}(1-x)LiMO{sub 2} electrode surfaces (M=Mn, Ni, Co) with mildly acidic, fluorinated solutions.
First-Principles Calculations, Electrochemical and X-ray Absorption Studies of Li-Ni-PO4 Surface-Treated xLi2MnO3 (1 x)LiMO2 (M = Mn, Ni, Co) Electrodes for Li-Ion Batteries