EFFECT OF CHEMISTRY VARIATIONS IN PLATE AND WELD FILLER METAL ON THE CORROSION PERFORMANCE OF NI-CR-MO ALLOYS
The ASTM standard B 575 provides the requirements for the chemical composition of Nickel-Chromium-Molybdenum (Ni-Cr-Mo) alloys such as Alloy 22 (N06022) and Alloy 686 (N06686). The compositions of each element are given in a range. For example, the content of Mo is specified from 12.5 to 14.5 weight percent for Alloy 22 and from 15.0 to 17.0 weight percent for Alloy 686. It was important to determine how the corrosion rate of welded plates of Alloy 22 using Alloy 686 weld filler metal would change if heats of these alloys were prepared using several variations in the composition of the elements even though still in the range specified in B 575. All the material used in this report were especially prepared at Allegheny Ludlum Co. Seven heats of plate were welded with seven heats of wire. Immersion corrosion tests were conducted in a boiling solution of sulfuric acid plus ferric sulfate (ASTM G 28 A) using both as-welded (ASW) coupons and solution heat-treated (SHT) coupons. Results show that the corrosion rate was not affected by the chemistry of the materials in the range of the standards.
- Research Organization:
- Yucca Mountain Project, Las Vegas, NV (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- NA
- OSTI ID:
- 886042
- Report Number(s):
- UCRL-PROC-218703; MOL.20060505.0154, DC#47514; TRN: US200616%%838
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Chemistry Variations in Plate and Weld Filler Metal on the Corrosion Performance of Ni-Cr-Mo Alloys
Localized Corrosion of Alloy 22 -Fabrication Effects-