Morphological and Mechanical Properties of Polypropylene[PP]/Poly(Ethylene Vinyl Acetate)[EVA] Blends. I. Homopolymer PP/Eva Systems
Journal Article
·
· Polymer Engineering and Science
Morphological and mechanical properties of polypropylene [PP]/poly(ethylene vinyl acetate) [EVA] blends have been studied. Infrared results using thin films first indicated a transition toward compatibility between both components at concentrations above 40% EVA. The transition was verified with different experimental techniques and it was associated to morphological changes and mechanical properties. The PP/EVA blends were mechanically evaluated in terms of impact and tensile strength to determine the influence of blending on the performance properties of these materials. Agreement was found between the transition and the enhancement of both elongation at break and impact strength.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 829318
- Report Number(s):
- P01-109983; TRN: US200610%%758
- Journal Information:
- Polymer Engineering and Science, Vol. 40, Issue 10
- Country of Publication:
- United States
- Language:
- English
Similar Records
Rheology, Mechanical Properties and Morphology of Poly(lactic acid)/Ethylene Vinyl Acetate Blends
Investigation on the Influence of EVA Content on the Mechanical and Thermal Characteristics of Poly(lactic acid) Blends
Preparation and characterization of reactive blends of poly(lactic acid), poly(ethylene-co-vinyl alcohol), and poly(ethylene-co-glycidyl methacrylate)
Journal Article
·
Mon Jul 01 00:00:00 EDT 2019
· Journal of Polymers and the Environment
·
OSTI ID:829318
+5 more
Investigation on the Influence of EVA Content on the Mechanical and Thermal Characteristics of Poly(lactic acid) Blends
Journal Article
·
Mon Jan 15 00:00:00 EST 2018
· Journal of Polymers and the Environment
·
OSTI ID:829318
Preparation and characterization of reactive blends of poly(lactic acid), poly(ethylene-co-vinyl alcohol), and poly(ethylene-co-glycidyl methacrylate)
Journal Article
·
Fri May 22 00:00:00 EDT 2015
· AIP Conference Proceedings
·
OSTI ID:829318