IMPROVEMENT OF WEAR COMPONENT'S PERFORMANCE BY UTILIZING ADVANCED MATERIALS AND NEW MANUFACTURING TECHNOLOGIES: CASTCON PROCESS FOR MINING APPLICATIONS
During this reporting period, the debinding and off-gassing furnace was switched from a vacuum furnace to a conventional kiln to solve the HIP can expansion problem during high temperature off-gassing, which caused disc distortion. Two 6.5 inch discs were produced. Both looked acceptable and one was machined. It was found that the disc hub section was little bit thin and micro cracks were seen along the disc radial directions.
- Research Organization:
- Michigan Technological University (US)
- Sponsoring Organization:
- (US)
- DOE Contract Number:
- FC26-01NT41055
- OSTI ID:
- 823833
- Resource Relation:
- Other Information: PBD: 22 Mar 2004
- Country of Publication:
- United States
- Language:
- English
Similar Records
IMPROVEMENT OF WEAR COMPONENT'S PERFORMANCE BY UTILIZING ADVANCED MATERIALS AND NEW MANUFACTURING TECHNOLOGIES: CASTCON PROCESS FOR MINING APPLICATIONS
IMPROVEMENT OF WEAR COMPONENT'S PERFORMANCE BY UTILIZING ADVANCED MATERIALS AND NEW MANUFACTURING TECHNOLOGIES: CASTCON PROCESS FOR MINING APPLICATIONS
IMPROVEMENT OF WEAR COMPONENT'S PERFORMANCE BY UTILIZING ADVANCED MATERIALS AND NEW MANUFACTURING TECHNOLOGIES: CASTCON PROCESS FOR MINING APPLICATIONS
Technical Report
·
Thu Mar 18 00:00:00 EST 2004
·
OSTI ID:823833
IMPROVEMENT OF WEAR COMPONENT'S PERFORMANCE BY UTILIZING ADVANCED MATERIALS AND NEW MANUFACTURING TECHNOLOGIES: CASTCON PROCESS FOR MINING APPLICATIONS
Technical Report
·
Thu May 01 00:00:00 EDT 2003
·
OSTI ID:823833
IMPROVEMENT OF WEAR COMPONENT'S PERFORMANCE BY UTILIZING ADVANCED MATERIALS AND NEW MANUFACTURING TECHNOLOGIES: CASTCON PROCESS FOR MINING APPLICATIONS
Technical Report
·
Thu Feb 27 00:00:00 EST 2003
·
OSTI ID:823833