Comparison of the electrochemical properties of several commercial graphites with a templated disordered carbon
Conference
·
OSTI ID:752627
A templated carbon was prepared by the pyrolysis of pyrene impregnated into pillared clay (PILC). The electrochemical performance of this was evaluated with the goal of using this material as an anode in Li-ion cells. The reversible capacity was measured as a function of C rate and the cycling characteristics were determined for various intercalation protocols. The performance of this material was compared to that of several commercial graphites tested under the same conditions. The PILC carbon shows great promise as a Li-ion anode if the fade and first-cycle losses can be controlled.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Sandia National Lab. (SNL-CA), Livermore, CA (United States)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 752627
- Report Number(s):
- SAND99-3017C; TRN: AH200018%%88
- Resource Relation:
- Conference: 38th Power Sources Conference, Cherry Hill, NJ (US), 06/12/2000--06/15/2000; Other Information: PBD: 22 Mar 2000
- Country of Publication:
- United States
- Language:
- English
Similar Records
Comparison of the electrochemical properties of several commercial graphites with a templated disordered carbon
Small angle neutron and X-ray scattering studies of carbons prepared using inorganic templates
Small angle neutron scattering characterization of the porous structure of carbons prepared using inorganic templates
Conference
·
Tue Apr 11 00:00:00 EDT 2000
·
OSTI ID:752627
Small angle neutron and X-ray scattering studies of carbons prepared using inorganic templates
Conference
·
Mon Sep 01 00:00:00 EDT 1997
·
OSTI ID:752627
+1 more
Small angle neutron scattering characterization of the porous structure of carbons prepared using inorganic templates
Journal Article
·
Mon Feb 01 00:00:00 EST 1999
· Chemistry of Materials
·
OSTI ID:752627
+1 more