Composite materials: Fatigue and fracture. Vol. 3. ASTM Special Technical Publication, No. 1110
- U.S. Army, Aerostructures Directorate (United States) NASA, Langley Research Center, Hampton, VA (United States)
The present volume discusses topics in the fields of matrix cracking and delamination, interlaminar fracture toughness, delamination analysis, strength and impact characteristics, and fatigue and fracture behavior. Attention is given to cooling rate effects in carbon-reinforced PEEK, the effect of porosity on flange-web corner strength, mode II delamination in toughened composites, the combined effect of matrix cracking and free edge delamination, and a 3D stress analysis of plain weave composites. Also discussed are the compression behavior of composites, damage-based notched-strength modeling, fatigue failure processes in aligned carbon-epoxy laminates, and the thermomechanical fatigue of a quasi-isotropic metal-matrix composite.
- OSTI ID:
- 7039421
- Country of Publication:
- United States
- Language:
- English
Similar Records
Composite materials - fatigue and fracture; Proceedings of the Symposium, Dallas, TX, October 24, 25, 1984
Residual strength determination due to fatigue loading by fracture mechanics in notched composite materials
Related Subjects
COMPOSITE MATERIALS
MECHANICAL PROPERTIES
CARBON FIBERS
COMPRESSION
CRACK PROPAGATION
CRACKS
DEFORMATION
EPOXIDES
FATIGUE
FRACTURE MECHANICS
FRACTURE PROPERTIES
IMPACT STRENGTH
IMPACT TESTS
KETONES
LAYERS
LEADING ABSTRACT
MATHEMATICAL MODELS
MATRIX MATERIALS
METALS
POLYMERS
POROSITY
STRESS ANALYSIS
THERMOMECHANICAL TREATMENTS
ABSTRACTS
DOCUMENT TYPES
ELEMENTS
FABRICATION
FIBERS
HEAT TREATMENTS
MATERIALS
MATERIALS TESTING
MATERIALS WORKING
MECHANICAL TESTS
MECHANICS
ORGANIC COMPOUNDS
ORGANIC OXYGEN COMPOUNDS
TESTING
360603* - Materials- Properties