Nanocrystallization and phase transformation in monodispersed ultrafine zirconia particles from various homogeneous precipitation methods
- Oak Ridge National Lab., TN (United States)
Monodispersed ultrafine (nano- to micrometer) zirconia precursor powders were synthesized by three different physicochemical methods: (1) forced hydrolysis, (2) homogeneous precipitation in inorganic salt solutions, and (3) hydrolysis/condensation of alkoxide. The forced hydrolysis method produced monoclinic nanocrystalline particles (cube shaped) of nanometer scale, which depended largely on the initial salt concentration. Methods 2 and 3, both involving the use of alcohol as a solvent, exhibited a faster particle formation rate and generated amorphous ultrafine (submicrometer) monodispersed microspheres, indicating that the presence of alcohol may have stimulated particle nucleation due to its low dielectric property (and, thus, the low solubility of nucleus species in mixed water-alcohol solutions). Nucleation and growth of the particles in solutions are discussed based on the measurements obtained by small-angle X-ray scattering (SAXS) and dynamic light scattering (DLS). High-temperature X-ray diffraction (HTXRD) and TGA/DTA studies elucidated the differences in phase transformation for different types of powders. The most interesting finding was the nonconventional monoclinic nanocrystal nucleation and growth that occurred prior to transformation to the tetragonal phase (at 1,200 C) during the heat treatment of the nanocrystalline powders produced by the forced hydrolysis.
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC05-96OR22464
- OSTI ID:
- 684421
- Journal Information:
- Journal of the American Ceramic Society, Vol. 82, Issue 9; Other Information: PBD: Sep 1999
- Country of Publication:
- United States
- Language:
- English
Similar Records
Methods for producing monodispersed particles of barium titanate
Growth mechanism of monodispersed ZrO/sub 2/ particles