Surface Properties of Photo-Oxidized Bituminous Coals: Final report
Natural weathering has a detrimental effect on the hydrophobic nature of coal, which in turn can influence clean-coal recovery during flotation. Few techniques are available that can establish the quality of coal surfaces and that have a short analysis time to provide input for process control. Luminescence emissions which can be quantified with an optical microscope and photometer system, are measurably influenced by degree of weathering as well as by mild storage deterioration. In addition, it has been shown that when vitrinite is irradiated with a relatively high intensity flux of violet- or ultraviolet- light in the presence of air, photo-oxidation of the surface occurs. The combination of measuring the change in luminescence emission intensity with degree of surface oxidation provided the impetus for the current investigation. The principal aim of this research was to determine whether clear correlations could be established among surface oxygen functionality, hydrophobicity induced by photo-oxidation, and measurements of luminescence intensity and alteration. If successful, the project would result in quantitative luminescence techniques based on optical microscopy that would provide a measure of the changes in surface properties as a function of oxidation and relate them to coal cleanability. Two analytical techniques were designed to achieve these goals. Polished surfaces of vitrain bands or a narrow size fraction of powdered vitrain concentrates were photo-oxidized using violet or ultraviolet light fluxes and then changes in surface properties and chemistry were measured using a variety of near-surface analytical techniques. Results from this investigation demonstrate that quantitative luminescence intensity measurements can be performed on fracture surfaces of bituminous rank coals (vitrains) and that the data obtained do reveal significant variations depending upon the level of surface oxidation. Photo-oxidation induced by violet or ultraviolet light fluxes does result in a progressive and significant increase in the amount of near-surface oxygen concentration at about the same level regardless of bituminous coal rank. These incremental changes in oxygen concentration appear to lower the hydrophobicity as shown by contact angle measurements on polished surfaces. Although this influence diminished as coal rank increased, the level of oxygen uptake was about the same, suggesting that the type of oxygen functionality formed during oxidation may be of great importance in modifying surface hydrophobicity. Changes in functional-group chemistry, measured by a variety of near-surface techniques, showed a general increase in the concentration of carbonyl-containing groups while those of CH{sub 2} groups decreased. All of these observations follow the trends observed in previous investigations of naturally weathered coals. The photo-oxidation technique also resulted in the development of phenolic, ester and anhydride moieties instead of the expected emplacement of carboxylic acid groups which are normally associated with naturally weathered coals. The importance of this observation is that esters and anhydrides would result in a more hydrophobic surface in comparison to the more hydrophilic surface resulting from acid functionality. This observation is consistent with the results of film flotation of UV-irradiated powdered vitrain in which floatability was generally observed to increase with increasing photo- oxidation.
- Research Organization:
- USDOE Federal Energy Technology Center, Morgantown, WV (United States)
- Sponsoring Organization:
- USDOE Assistant Secretary for Fossil Energy, Washington, DC (United States)
- DOE Contract Number:
- FG22-93PC93223
- OSTI ID:
- 675002
- Report Number(s):
- DOE/PC/93223-14; ON: DE98058913
- Resource Relation:
- Other Information: PBD: 1998
- Country of Publication:
- United States
- Language:
- English
Similar Records
Surface properties of photo-oxidized bituminous coals. Technical progress report, October--December 1995
Surface properties of photo-oxidized bituminous coals. Technical progress report for the period April to June, 1996