Fabrication of a 1200 kg Ingot of V-4Cr-4Ti alloy for the DIII-D Radiative Divertor Program
Vanadium chromium titanium alloys are attractive materials for fusion reactors because of their high temperature capability and their potential for low neutron active and rapid activation decay. A V-4Cr-4Ti alloy has been selected in the U.S. as the current leading candidate vanadium alloy for future use in fusion reactor structural applications. General Atomics (GA), in conjunction with the Department of Energy`s (DOE) DIII-D Program, is carrying out a plan for the utilization of this vanadium alloy in the DIII-D tokamak. The plan will culminate in the fabrication, installation, and operation of a V-4Ti alloy structure in the DIII-D Radiative Divertor (RD) upgrade. The deployment of vanadium alloy will provide a meaningful step in the development and technology acceptance of this advanced material for future fusion power devices. Under a GA contract and material specification, an industrial scale 1200 kg heat (ingot) of a V-4Cr-4Ti alloy has been produced and converted into product forms by Wah Chang of Albany, Oregon (WCA). To assure the proper control of minor and trace impurities which affect the mechanical and activation behavior of this vanadium alloy, selected lots of raw vanadium base metal were processed by aluminothermic reduction of high purity vanadium oxide, and were then electron beam melted into two high purity vanadium ingots. The ingots were then consolidated with high purity Cr and Ti, and double vacuum-arc melted to obtain a 1200 kg V-4Cr-4Ti alloy ingot. Several billets were extruded from the ingot, and were then fabricated into plate, sheet, and rod at WCA. Tubing was subsequently processed from plate material. The chemistry and fabrication procedures for the product forms were specified on the basis of experience and knowledge gained from DOE Fusion Materials Program studies on previous laboratory scale heats and a large scale ingot (500 kg)
- Research Organization:
- General Atomics, San Diego, CA (United States)
- Sponsoring Organization:
- USDOE Office of Energy Research, Washington, DC (United States)
- DOE Contract Number:
- AC03-89ER51114
- OSTI ID:
- 629290
- Report Number(s):
- GA-A22740; CONF-971090-; ON: DE98002633; TRN: 98:009743
- Resource Relation:
- Conference: 8. international conference on fusion reactor materials (ICFRM), Sendai (Japan), 26-31 Oct 1997; Other Information: PBD: [Jan 1998]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Tensile and impact properties of V-4Cr-4Ti alloy heats 832665 and 832864.
Fabrication of 500-kg heat of V-4Cr-4Ti