Development of elements of a high-Tc superconducting cable. Quarterly report, 1 Jul-30 Sep 91
Technical Report
·
OSTI ID:6016802
The program is aimed at the development of long lengths of silver-clad BSCCO. The material of choice is BSCCO-2223 with 20K the operating temperature goal. Such a tape conductor ultimately could be used in a coil for a magnet, motor or generator. The program is designed to tackle several key problems with parallel tasks. A large variety of BSCCO powders are under investigation. Silver tubes are packed with superconductor powder and deformed to form tape conductors. An alternate method of making silver-encapsulated superconducting tape is also being pursued. Variations in the powders and processing parameters are used to optimize the tape Jc.
- Research Organization:
- General Electric Co., Schenectady, NY (United States). Corporate Research and Development Center
- OSTI ID:
- 6016802
- Report Number(s):
- AD-A-242479/4/XAB; CNN: N00014-88-C-0681
- Country of Publication:
- United States
- Language:
- English
Similar Records
Development of elements of a high-Tc superconducting cable. Annual report, 1 Jul 90-30 Jun 91
Development of elements of a high-Tc superconducting cable. Rept. for 1 Jan-31 Mar 91
Development of elements of a high Tc superconducting cable. Annual report, 1 July 1991-30 June 1992
Technical Report
·
Sun Jun 30 00:00:00 EDT 1991
·
OSTI ID:6016802
Development of elements of a high-Tc superconducting cable. Rept. for 1 Jan-31 Mar 91
Technical Report
·
Sun Mar 31 00:00:00 EST 1991
·
OSTI ID:6016802
Development of elements of a high Tc superconducting cable. Annual report, 1 July 1991-30 June 1992
Technical Report
·
Wed Jan 01 00:00:00 EST 1992
·
OSTI ID:6016802
Related Subjects
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
SUPERCONDUCTING CABLES
FABRICATION
BISMUTH OXIDES
CALCIUM OXIDES
COPPER OXIDES
CRITICAL TEMPERATURE
HIGH-TC SUPERCONDUCTORS
POWDERS
PROCESSING
SILVER
STRONTIUM OXIDES
SUPERCONDUCTING MAGNETS
SUPERCONDUCTING MOTORS
TEMPERATURE RANGE 0013-0065 K
TRANSITION TEMPERATURE
ALKALINE EARTH METAL COMPOUNDS
BISMUTH COMPOUNDS
CABLES
CALCIUM COMPOUNDS
CHALCOGENIDES
CONDUCTOR DEVICES
COPPER COMPOUNDS
ELECTRIC CABLES
ELECTRIC MOTORS
ELECTRICAL EQUIPMENT
ELECTROMAGNETS
ELEMENTS
EQUIPMENT
MAGNETS
METALS
MOTORS
OXIDES
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
STRONTIUM COMPOUNDS
SUPERCONDUCTING DEVICES
SUPERCONDUCTORS
TEMPERATURE RANGE
THERMODYNAMIC PROPERTIES
TRANSITION ELEMENT COMPOUNDS
TRANSITION ELEMENTS
665412* - Superconducting Devices- (1992-)
SUPERCONDUCTIVITY AND SUPERFLUIDITY
SUPERCONDUCTING CABLES
FABRICATION
BISMUTH OXIDES
CALCIUM OXIDES
COPPER OXIDES
CRITICAL TEMPERATURE
HIGH-TC SUPERCONDUCTORS
POWDERS
PROCESSING
SILVER
STRONTIUM OXIDES
SUPERCONDUCTING MAGNETS
SUPERCONDUCTING MOTORS
TEMPERATURE RANGE 0013-0065 K
TRANSITION TEMPERATURE
ALKALINE EARTH METAL COMPOUNDS
BISMUTH COMPOUNDS
CABLES
CALCIUM COMPOUNDS
CHALCOGENIDES
CONDUCTOR DEVICES
COPPER COMPOUNDS
ELECTRIC CABLES
ELECTRIC MOTORS
ELECTRICAL EQUIPMENT
ELECTROMAGNETS
ELEMENTS
EQUIPMENT
MAGNETS
METALS
MOTORS
OXIDES
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
STRONTIUM COMPOUNDS
SUPERCONDUCTING DEVICES
SUPERCONDUCTORS
TEMPERATURE RANGE
THERMODYNAMIC PROPERTIES
TRANSITION ELEMENT COMPOUNDS
TRANSITION ELEMENTS
665412* - Superconducting Devices- (1992-)