Tests of periclase-carbon refractories in an arc steel-melting furnace
Journal Article
·
· Refractories (Engl. Transl.); (United States)
OSTI ID:5459686
An experimental lot of unfired periclase-carbon parts was produced and tested in a DSP-25 arc steel melting furnace. The average wear rate of the experimental parts was 30% less than for PKhS parts and with a decrease in the lining thickness from 460 to 230 mm the wear rate dropped by 2-2.5 times. During service a complex infiltration-metasomatic zonality if formed. The metasomatism has an iron-silicate character. The wear of the periclase-carbon parts occurs primarily by fusion of the decarburized subzone of the working zone and of the scorified crust penetrated by silicates.
- Research Organization:
- Leningrad Soviet Polytechnic Institute
- OSTI ID:
- 5459686
- Journal Information:
- Refractories (Engl. Transl.); (United States), Vol. 26:10
- Country of Publication:
- United States
- Language:
- English
Similar Records
Life of refractories in service in a furnace for melting in a molten bath
Periclase-carbon products for electric steel furnaces
Use in open-hearth roofs of periclase-chromite parts made from electrofused periclase-chromite
Journal Article
·
Mon Sep 01 00:00:00 EDT 1986
· Refractories (Engl. Transl.); (United States)
·
OSTI ID:5459686
+3 more
Periclase-carbon products for electric steel furnaces
Journal Article
·
Thu Sep 01 00:00:00 EDT 1988
· Refractories (Engl. Transl.); (United States)
·
OSTI ID:5459686
+7 more
Use in open-hearth roofs of periclase-chromite parts made from electrofused periclase-chromite
Journal Article
·
Sat Mar 01 00:00:00 EST 1986
· Refractories (Engl. Transl.); (United States)
·
OSTI ID:5459686
+3 more
Related Subjects
36 MATERIALS SCIENCE
32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATION
ARC FURNACES
LINERS
MATERIALS TESTING
TEMPERATURE EFFECTS
THERMAL CYCLING
REFRACTORIES
STEELS
MELTING
CHEMICAL COMPOSITION
COMPRESSION STRENGTH
DECARBURIZATION
GRAPHITE
MAGNESIUM OXIDES
OXIDE MINERALS
THERMAL DEGRADATION
THERMAL EFFICIENCY
WEAR RESISTANCE
ALKALINE EARTH METAL COMPOUNDS
ALLOYS
CARBON
CHALCOGENIDES
CHEMICAL REACTIONS
EFFICIENCY
ELECTRIC FURNACES
ELEMENTAL MINERALS
ELEMENTS
FURNACES
IRON ALLOYS
IRON BASE ALLOYS
MAGNESIUM COMPOUNDS
MECHANICAL PROPERTIES
MINERALS
NONMETALS
OXIDES
OXYGEN COMPOUNDS
PHASE TRANSFORMATIONS
TESTING
360204* - Ceramics
Cermets
& Refractories- Physical Properties
320302 - Energy Conservation
Consumption
& Utilization- Industrial & Agricultural Processes- Materials
360203 - Ceramics
Cermets
& Refractories- Mechanical Properties
32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATION
ARC FURNACES
LINERS
MATERIALS TESTING
TEMPERATURE EFFECTS
THERMAL CYCLING
REFRACTORIES
STEELS
MELTING
CHEMICAL COMPOSITION
COMPRESSION STRENGTH
DECARBURIZATION
GRAPHITE
MAGNESIUM OXIDES
OXIDE MINERALS
THERMAL DEGRADATION
THERMAL EFFICIENCY
WEAR RESISTANCE
ALKALINE EARTH METAL COMPOUNDS
ALLOYS
CARBON
CHALCOGENIDES
CHEMICAL REACTIONS
EFFICIENCY
ELECTRIC FURNACES
ELEMENTAL MINERALS
ELEMENTS
FURNACES
IRON ALLOYS
IRON BASE ALLOYS
MAGNESIUM COMPOUNDS
MECHANICAL PROPERTIES
MINERALS
NONMETALS
OXIDES
OXYGEN COMPOUNDS
PHASE TRANSFORMATIONS
TESTING
360204* - Ceramics
Cermets
& Refractories- Physical Properties
320302 - Energy Conservation
Consumption
& Utilization- Industrial & Agricultural Processes- Materials
360203 - Ceramics
Cermets
& Refractories- Mechanical Properties