304 BORIDED STAINLESS STEEL TENSILE DATA
Technical Report
·
OSTI ID:4826046
Forty borided stainless steel samples, both irradiated and unirradiated, were pulled. The samples were split into two groups according to their chemical composition and a representative number of samples from each group was pulled at room temperature, 400, 800, 1200, and 1600 deg F. The physical properties were measured and recorded. (auth)
- Research Organization:
- General Electric Co. Aircraft Nuclear Propulsion Dept., Idaho Falls, Idaho
- DOE Contract Number:
- AT(11-1)-171
- NSA Number:
- NSA-16-022648
- OSTI ID:
- 4826046
- Report Number(s):
- DC-60-2-726
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-62
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of Heat Treatment on Phase Transformation and Corrosion Resistance of Boride Layer on Austenitic Stainless Steel AISI 304
Effect of chemistry variations on the short-term rupture life and tensile properties of 20% cold-worked type 316 stainless steel. [LMFBR; FFTF]
In-situ high-energy X-ray characterization of neutron irradiated HT-UPS stainless steel under tensile deformation
Journal Article
·
Mon Oct 15 00:00:00 EDT 2018
· Metallurgical and Materials Transactions B, Process Metallurgy and Materials Processing Science
·
OSTI ID:4826046
Effect of chemistry variations on the short-term rupture life and tensile properties of 20% cold-worked type 316 stainless steel. [LMFBR; FFTF]
Journal Article
·
Fri Apr 01 00:00:00 EST 1977
· Nucl. Technol.; (United States)
·
OSTI ID:4826046
In-situ high-energy X-ray characterization of neutron irradiated HT-UPS stainless steel under tensile deformation
Journal Article
·
Fri Jul 06 00:00:00 EDT 2018
· Acta Materialia
·
OSTI ID:4826046
+5 more