Effect of ammonium diuranate precipitation conditions on the characteristics and sintering behaviour of uranium dioxide
Ammonium diurannte was prepared by adding aqueous ammonia to uranyl nitrate solution under different conditions of temperature and final pH. The resulting precipitates, when dried, can be considered as loosely bound compounds with an ammonia/uranium ratio of 0: 37 containing varying amounts of water and ammonium nitrate. As well as differing in composition, these precipitates differ markedly in their specific surface areas. After calcination to U3O8 in argon at 700 deg and reduction in hydrogen at the same temperature, all the diuranates yield uranium dioxide of similar specific surface, and it is concluded that the calcination temperature is the principal factor in determining this. The powders, when milled, mixed with an organic binding agent, granulated, pressed, and sintered in hydrogen for 2 hr at 1650 deg , give uranium dioxide compacts with bulk densities greater than 96.5% of the x-ray density (10.96 g/cm3). Little, if any, correlation was found between the precipitation conditions and the sintered densities of the compacts, although a relatively rapid rate of addition of ammonia seems to give a slightly denser compact and it seems possible that some uncontrolled variation during milling or pressing outweighs any effects due to differences between the powders.
- Research Organization:
- United Kingdom Atomic Energy Authority, Springfields, Lancs, Eng.
- Sponsoring Organization:
- USDOE
- NSA Number:
- NSA-17-008718
- OSTI ID:
- 4731695
- Journal Information:
- Journal of Applied Chemistry, Vol. 12, Issue 9; Other Information: Orig. Receipt Date: 31-DEC-63; ISSN 0021-8871
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
PREPARATION OF UO$sub 2$ FOR USE IN CERAMIC FUELS. PART II. CONTINUOUS PRECIPITATION OF AMMONIUM DIURANATE
THE SINTERING BEHAVIOUR AND STABILITY OF (PuU)O$sub 2$ SOLID SOLUTIONS