Solidification of particle-reinforced metal-matrix composites
- McMaster Univ., Hamilton, Ontario (Canada). Dept. of Materials Science and Engineering
The solidification behavior of ceramic particle-reinforced metal-matrix composites (MMCs) is different from that of the bare matrix, not only because of the presence of the ceramic particles, but also due to their redistribution in the melt that results in nonhomogeneous thermophysical properties. The MMCs comprised of 10- to 15-{micro}m SiC particles of varying volume fractions, dispersed uniformly in a modified aluminum A356 alloy by the melt stirring technique, were solidified unidirectionally in a thermocouple-instrumented cylindrical steel mold. The cooling rates were continually monitored by measuring temperatures at different depths in the melt, and the solidified MMCs were sectioned into disks and chemically analyzed for SiC volume fraction. The results point out that the cooling rate increased with increasing volume fraction of SiC particles. A small increase in the bulk SiC volume fraction of the cast MMC was observed due to particle settling during solidification. A one-dimensional enthalpy model of MMC solidification was formulated, wherein particle settling occurring in the solidifying matrix was coupled to the enthalpy equation by means of the Richardson-Zaki hindered settling correlation. A comparative study of simulations with experiments suggested that the thermal response of SiC particles used in this study was similar to that of single crystals, and their presence increased the effective thermal conductivity of the composite.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 367854
- Journal Information:
- Metallurgical Transactions, B, Vol. 27, Issue 4; Other Information: PBD: Aug 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Melting and casting characteristics of aluminum alloy A356-SiC particulate reinforced cast composites
Solidification of metal matrix composites; Proceedings of the Conference, Indianapolis, IN, Oct. 1-5, 1989