Synthesis and magnetic structure of the layered manganese oxide selenide Sr{sub 2}MnO{sub 2}Ag{sub 1.5}Se{sub 2}
- Department of Chemistry, University of Oxford, Inorganic Chemistry Laboratory, South Parks Road, Oxford OX1 3QR (United Kingdom)
The synthesis of a high-purity sample of the layered oxide selenide Sr{sub 2}MnO{sub 2}Ag{sub 1.5}Se{sub 2} is reported. At ambient temperature it crystallises in the space group I4/mmm with two formula units in the unit cell and lattice parameters a=4.08771(1) Å, c=19.13087(8) Å. The compound displays mixed-valent manganese in a formal oxidation state close to +2.5 and powder neutron diffraction measurements reveal that below the Néel temperature of 63(1) K this results in an antiferromagnetic structure which may be described as A-type, modelled in the magnetic space group P{sub I}4/mnc (128.410 in the Belov, Neronova and Smirnova (BNS) scheme) in which localised Mn moments of 3.99(2) μ{sub B} are arranged in ferromagnetic layers which are coupled antiferromagnetically. In contrast to the isostructural compound Sr{sub 2}MnO{sub 2}Cu{sub 1.5}S{sub 2}, Sr{sub 2}MnO{sub 2}Ag{sub 1.5}Se{sub 2} does not display long range ordering of coinage metal ions and vacancies, nor may significant amounts of the coinage metal readily be deintercalated using soft chemical methods. - Graphical abstract: Sr{sub 2}MnO{sub 2}Ag{sub 1.5}Se{sub 2} containing mixed valent Mn ions undergoes magnetic ordering with ferromagnetic coupling within MnO{sub 2} sheets and antiferromagnetic coupling between MnO{sub 2} sheets. - Highlights: • High purity sample of Sr{sub 2}MnO{sub 2}Ag{sub 1.5}Se{sub 2} obtained. • Magnetic structure determined. • Compared with related mixed-valent manganite oxide chalcogenides.
- OSTI ID:
- 22658142
- Journal Information:
- Journal of Solid State Chemistry, Vol. 245; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Enhanced ferromagnetic order in Sr{sub 4}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} featuring canted [MnO{sub 4}]{sub ∞} spin chains of mixed-valent Mn(III)/Mn(IV). Aliovalent substitution of the Sr{sub 4−x}Ln{sub x}Mn{sup III}{sub 2+x}Mn{sup IV}{sub 1−x}O{sub 3}(GeO{sub 4}){sub 3} solid-solution
Crystal structures and magnetic properties of Ca{sub 2{minus}x}Sr{sub x}MnO{sub 4}
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
36 MATERIALS SCIENCE
AMBIENT TEMPERATURE
COUPLING
EXPERIMENTAL DATA
LATTICE PARAMETERS
LAYERS
MAGNETIZATION
MANGANESE IONS
MANGANESE OXIDES
MANGANESE SELENIDES
NEUTRON DIFFRACTION
OXIDATION
SILVER COMPOUNDS
SPACE GROUPS
SYNTHESIS
TETRAGONAL LATTICES