Coexistence of negative photoconductivity and hysteresis in semiconducting graphene
- School of Physics, National Laboratory of Solid State Microstructures, and Collaborative Innovation Center of Advanced Microstructures, Nanjing University, No. 22 Hankou Road, Nanjing, Jiangsu, 210093 (China)
- Department of Materials Science and Engineering, National Laboratory of Solid State Microstructures, and Collaborative Innovation Center of Advanced Microstructures, No. 22 Hankou Road, Nanjing University, Nanjing, Jiangsu, 210093 (China)
- School of Physics Science and Technology, Yangzhou University, No. 180 Siwangting Road, Yangzhou, Jiangsu, 225002 (China)
Solution-processed graphene quantum dots (GQDs) possess a moderate bandgap, which make them a promising candidate for optoelectronics devices. However, negative photoconductivity (NPC) and hysteresis that happen in the photoelectric conversion process could be harmful to performance of the GQDs-based devices. So far, their origins and relations have remained elusive. Here, we investigate experimentally the origins of the NPC and hysteresis in GQDs. By comparing the hysteresis and photoconductance of GQDs under different relative humidity conditions, we are able to demonstrate that NPC and hysteresis coexist in GQDs and both are attributed to the carrier trapping effect of surface adsorbed moisture. We also demonstrate that GQDs could exhibit positive photoconductivity with three-order-of-magnitude reduction of hysteresis after a drying process and a subsequent encapsulation. Considering the pervasive moisture adsorption, our results may pave the way for a commercialization of semiconducting graphene-based and diverse solution-based optoelectronic devices.
- OSTI ID:
- 22611675
- Journal Information:
- AIP Advances, Vol. 6, Issue 4; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
Spatial confinement effects on ultrathin semiconducting polymer heterojunction thin films
Chiral Graphene Quantum Dots