Fabrication and characterization of pristine and annealed Ga doped ZnO thin films using sputtering
- Department of Applied Physics, Indian School of Mines, Dhanbad, Jharkhand-826004 (India)
- School of Electronics Engineering, KIIT University, Campus-3, Patia, Bhubaneswar, Odisha-751024 (India)
ZnO is a wide-band gap, transparent, polar semiconductor with unparalleled optoelectronic, piezoelectric, thermal and transport properties, which make it the material of choice for a wide range of applications such as blue/UV optoelectronics, energy conversion, transparent electronics, spintronic, plasmonic and sensor devices. We report, three sets of Ga doped Zinc Oxide (GZO) were fabricated in different sputtering power (100 watt, 200 watt and 300 watt). Thereafter films were annealed in nitrogen ambient for 30 minutes at 400° C. From the optical absorption spectroscopy it was found that pristine films are showing a 75% transmittance in the visible region of light and it increases after the annealing. However, for 300 W grown sample opposite trend has been achieved for the post annealed sample. X-ray diffraction pattern of all the pristine and annealed films showed a preferable growth orientation at (002) phase. Some other weak peaks were also appeared in different angle which indicates that films are polycrystalline in nature. XRD data also reveals that crystallite size increases with sputtering power up to 200 W and thereafter it decreases with the deposition power. It also noted that the crystallite size of the annealed film increases with compare to the non annealed films. At room temperature an enhancement in electrical properties of Ga doped ZnO thin films was noted for the annealed ZnO films except for the film deposited at 300 watt. More significantly, it was found that annealed thin films showed the resistivity in the range of 10{sup −3} ∼ 10{sup −4} ohm-cm. Such a high optical transmittance and conducting zinc-oxide thin film can be used as a window layer in solar cell.
- OSTI ID:
- 22606552
- Journal Information:
- AIP Conference Proceedings, Vol. 1728, Issue 1; Conference: ICC 2015: International conference on condensed matter and applied physics, Bikaner (India), 30-31 Oct 2015; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Radio-Frequency Superimposed Direct Current Magnetron Sputtered Ga:ZnO Transparent Conducting Thin Films
Combinatorial characterization of transparent conductive properties of Ga-doped ZnO films cosputtered from electron cyclotron resonance and rf magnetron plasma sources
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ABSORPTION
ABSORPTION SPECTROSCOPY
ANNEALING
DOPED MATERIALS
ELECTRICAL PROPERTIES
ENERGY CONVERSION
GALLIUM ADDITIONS
LAYERS
PIEZOELECTRICITY
POLYCRYSTALS
SEMICONDUCTOR MATERIALS
SENSORS
SOLAR CELLS
SPUTTERING
TEMPERATURE RANGE 0273-0400 K
THIN FILMS
VISIBLE RADIATION
X RADIATION
X-RAY DIFFRACTION
ZINC OXIDES