Evolution of microstructure and grain boundary character distribution of a tin bronze annealed at different temperatures
- College of Materials Science and Engineering, Chongqing University of Technology, Chongqing 400054 (China)
- Faculty of Materials and Energy, Southwest University, Chongqing 400715 (China)
Specimens cut from a rolled tin bronze sheet were annealed at 400–800 °C for 1 h and evolution of their microstructures was then characterized in details by electron channeling contrast imaging and electron backscatter diffraction techniques. Particularly, statistics on special boundaries (SBs) with Σ ≤ 29 and network connectivity of random high angle boundaries (HABs) in the annealed specimens were examined to probe optimization potentials of grain boundary character distribution (GBCD) for this material. Results show that the deformed microstructure in the as-received material begins to be recrystallized when the annealing temperature increase to 500 °C and average grain sizes surge with further increasing temperatures. As a result of the recrystallization, a large number of annealing twins (with Σ3 misorientation) are produced, leading to remarkably increased fractions of SBs (f{sub SBs}). Thanks to preexisting dense low angle boundaries, the majority of SBs in the 500 °C specimen with only partial recrystallization are Σ3{sub ic} (incoherent) boundaries, which effectively disrupt connectivity of random HABs network. Although the f{sub SBs} can be further increased (up to 72.5%) in specimens with full recrystallization (at higher temperatures), the Σ3{sub ic} boundaries would be replaced to some extent by Σ3{sub c} (coherent) boundaries which do not contribute directly to optimizing the GBCD. This work should be able to provide clear suggestions on applying the concept of grain boundary engineering to tin bronze alloys. - Highlights: • The rolled tin bronze begins to be recrystallized as temperature increases to 500 °C. • A lot of SBs are produced after recrystallization and the highest f{sub SBs} is 72.5%. • Partially recrystallized specimen has the optimum GBCD due to more Σ3{sub ic} boundaries. • The Σ3{sub ic} boundaries are replaced by Σ3{sub c} boundaries after full recrystallization.
- OSTI ID:
- 22587138
- Journal Information:
- Materials Characterization, Vol. 114; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
Evolution of Σ3n CSL boundaries in Ni-Cr-Mo alloy during aging treatment
Role of twinning in the optimization of the grain boundary character distribution