Isothermal sections of the quasi-ternary systems Ag{sub 2}S(Se)–Ga{sub 2}S(Se){sub 3}–In{sub 2}S(Se){sub 3} at 820 K and the physical properties of the ternary phases Ga{sub 5.5}In{sub 4.5}S{sub 15}, Ga{sub 6}In{sub 4}Se{sub 15} and Ga{sub 5.5}In{sub 4.5}S{sub 15}:Er{sup 3+}, Ga{sub 6}In{sub 4}Se{sub 15}:Er{sup 3+}
- Department of Ecology and Environmental Protection, Eastern European National University, Lutsk (Ukraine)
- Department of General Physics, Eastern European National University, Lutsk (Ukraine)
- Department of Inorganic and Physical Chemistry, Eastern European National University, Lutsk (Ukraine)
Isothermal sections of the quasi-ternary systems Ag{sub 2}S(Se)–Ga{sub 2}S(Se){sub 3}–In{sub 2}S(Se){sub 3} at 820 K were compared. Along the 50 mol% Ag{sub 2}S(Se), both systems feature continuous solid solutions with the chalcopyrite structure. Along the 17 mol% Ag{sub 2}S(Se), the interactions at the AgIn{sub 5}S(Se){sub 8}–'AgGa{sub 5}S(Se){sub 8}' sections are different. In the Ag{sub 2}S–Ga{sub 2}S{sub 3}–In{sub 2}S{sub 3} system the existence of the layered phase AgGa{sub x}In{sub 5–x}S{sub 8}, 2.25≤x≤2.85, was confirmed (S.G. P6{sub 3}mc). The Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} system features the formation of solid solution (up to 53 mol% Ga{sub 2}Se{sub 3}) based on AgIn{sub 5}Se{sub 8} (S.G. P-42m). Crystal structure, atomic coordinates were determined by powder diffraction method for samples from the homogeneity region of AgIn{sub 5}Se{sub 8}. Specific conductivities of the crystals Ga{sub 6}In{sub 4}Se{sub 15} (1.33·10{sup −6} Ω{sup −1} m{sup −1}), Ga{sub 5.94}In{sub 3.96}Er{sub 0.1}Se{sub 15} (3.17·10{sup −6} Ω{sup −1} m{sup −1}), Ga{sub 5.5}In{sub 4.5}S{sub 15} (7.94·10{sup −6} Ω{sup −1} m{sup −1}), Ga{sub 5.46}In{sub 4.47}Er{sub 0.07}S{sub 15} (1·10{sup −9} Ω{sup −1} m{sup −1}) were measured at room temperature. Optical absorption and photoconductivity spectra were recorded in the range 400–760 nm. The introduction of erbium leads to an increase in the absorption coefficient and to the appearance of absorption bands at 530, 660, 810, 980, 1530 nm. - Highlights: • Nature of solid solutions in Ag{sub 2}S(Se)–Ga{sub 2}S(Se){sub 3}–In{sub 2}S(Se){sub 3} (820 K) were discussed. • Crystal structures of ternary and quaternary compounds were discussed. • Specific conductivity, optical properties of four single crystals were measured. • Photoconductivity of the Ga{sub 5.5}In{sub 4.5}S{sub 15} in the range 400–760 nm were recorded.
- OSTI ID:
- 22584062
- Journal Information:
- Journal of Solid State Chemistry, Vol. 237; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Phase equilibria in the quasiternary system Ag{sub 2}S–Ga{sub 2}S{sub 3}–In{sub 2}S{sub 3} and optical properties of (Ga{sub 55}In{sub 45}){sub 2}S{sub 300}, (Ga{sub 54.59}In{sub 44.66}Er{sub 0.75}){sub 2}S{sub 300} single crystals
Synthesis, structure, and electronic structure of CsAgGa{sub 2}Se{sub 4}
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ABSORPTION
CHALCOPYRITE
COMPARATIVE EVALUATIONS
GALLIUM SELENIDES
GALLIUM SULFIDES
HEXAGONAL LATTICES
INDIUM SELENIDES
INDIUM SULFIDES
INTERACTIONS
MONOCRYSTALS
OPTICAL PROPERTIES
PHOTOCONDUCTIVITY
PHOTOVOLTAIC EFFECT
POWDERS
QUATERNARY ALLOY SYSTEMS
SILVER SELENIDES
SILVER SULFIDES
SOLID SOLUTIONS
SPECTRA
X-RAY DIFFRACTION