Order–disorder phase transition in the antiperovskite-type structure of synthetic kogarkoite, Na{sub 3}SO{sub 4}F
- Department of Crystallography, Institute of Earth Sciences, St. Petersburg State University, University Emb. 7/9, 199034 St. Petersburg (Russian Federation)
High-temperature phase transition of synthetic kogarkoite, Na{sub 3}SO{sub 4}F, has been studied by high-temperature X-ray powder and single-crystal diffraction. The temperature of the phase transition can be estimated as 112.5±12.5 °C. The low-temperature phase, α-Na{sub 3}SO{sub 4}F, at 293 K, is monoclinic, P2{sub 1}/m, a=18.065(3), b=6.958(1), c=11.446(1) Å, β=107.711(1)°, Z=12. The structure contains thirteen symmetrically independent Na sites with coordination numbers varying from 6 to 8, and six independent S sites. The high-temperature β-phase at 423 K is rhombohedral, R-3m, a=6.94(1), c=24.58(4) Å, Z=9. The crystal structure of both polymorphs of Na{sub 3}SO{sub 4}F can be described as a 9R antiperovskite polytype based upon triplets of face-sharing [FNa{sub 6}] octahedra linked into a three-dimensional framework by sharing corners. In the α-modification, the SO{sub 4} tetrahedra are completely ordered and located in the framework cavities. In the β-modification, there are only two symmetrically independent Na atoms in the structure. The main difference between the structures of the α- and β-phases is the degree of ordering of the SO{sub 4} tetrahedra: in the α-modification, they are completely ordered, whereas, in the β-modification, the complete disorder is observed, which is manifested in a number of low-occupied O sites around fully occupied S sites. The phase transition is therefore has an order–disorder character and is associated with the decrease of structural complexity measured as an information content per unit cell [577.528 bits for the low- (α) and 154.830 bits for the high- (β) temperature modifications]. - Graphical abstract: High-temperature phase transition of synthetic kogarkoite, Na{sub 3}SO{sub 4}F, revealed the existence of the monoclinic-to-rhombohedral phase transition at 112.5±12.5 °C. The phase transition has an order–disorder character and is associated with the decrease of structural complexity. - Highlights: • Phase transition in Na{sub 3}SO{sub 4}F (kogarkoite) has an order–disorder character. • Antiperovskite framework of F-centered octahedra has a high stability. • Information-based structural complexity decreases across the phase transition.
- OSTI ID:
- 22573925
- Journal Information:
- Journal of Solid State Chemistry, Vol. 231; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structure and properties of α-NaFeO{sub 2}-type ternary sodium iridates
Dipole ordering and ionic conductivity in NASICON-Type Na{sub 3}Cr{sub 2}(PO{sub 4}){sub 3} structures