Effect of alloying by lanthanum and high rhenium superalloys on the basis of Ni-Al-Cr on the structure and phase composition
- Tomsk State University of Architecture and Building, 2, Solyanaya Sq., 634003, Tomsk (Russian Federation)
- Institute of Strength Physics and Materials Science, SB RAS, 2/4, Academicheskii Av., 634055, Tomsk (Russian Federation)
This paper presents transmission and scanning electronic microscope investigations of Ni-Al-Cr superalloy alloyed with additional Re and La elements. This superalloy is obtained by the directional solidification method and subsequently is subjected to two-stage high-temperature annealing: 1) at T = 1150°C, the test time is 1 hour; 2) at T = 1100°C, the testing time is 1430 hours. It was found that the γ- and γ′-phases are the main phases in the two states on the basis of fcc lattice. Where γ is the disordered fcc solid solution and γ′-phase is the main phase with an ordered arrangement of atoms having the L1{sub 2} superstructure. It is shown that such additional elements as Re and La result in the formation of new phases in Ni-Al-Cr accompanied by considerable modifications of quasi-cuboid structure in its γ′-phase. The phase composition and morphology of the phases are studied.
- OSTI ID:
- 22494427
- Journal Information:
- AIP Conference Proceedings, Vol. 1698, Issue 1; Conference: AMTC-2015: 2. all-Russian scientific conference of young scientists on advanced materials in technology and construction, Tomsk (Russian Federation), 6-9 Oct 2015; Other Information: (c) 2016 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Elements distribution and deformation features of a 4.5% Re nickel-based single crystal superalloy during creep at high temperature
Design of Novel Precipitate-Strengthened Al-Co-Cr-Fe-Nb-Ni High-Entropy Superalloys