Effect of 50MeV Li{sup 3+} ion irradiation on structural, optical and electrical properties of amorphous Se{sub 95}Zn{sub 5} thin films
Present work focuses on the effect of swift heavy ion (SHI) irradiation of 50MeV Li{sup 3+} ions by varying the fluencies in the range of 1×10{sup 12} to 5×10{sup 13} ions/cm{sup 2} on the morphological, structural, optical and electrical properties of amorphous Se{sub 95}Zn{sub 5} thin films. Thin films of ~250nm thickness were deposited on cleaned glass substrates by thermal evaporation technique. X-ray diffraction (XRD) analysis shows the pristine thin film of Se{sub 95}Zn{sub 5} growsin hexagonal phase structure. Also it was found that the small peak observed in XRD spectra vanishes after SHI irradiation indicates the defects of the material increases. The optical parameters: absorption coefficient (α), extinction coefficient (K), refractive index (n) optical band gap (E{sub g}) and Urbach’s energy (E{sub U}) are determined from optical absorption spectra data measured from spectrophotometry in the wavelength range 200-1000nm. It was found that the values of absorption coefficient, refractive index and extinction coefficient increases while the value optical band gap decreases with the increase of ion fluence. This post irradiation change in the optical parameters was interpreted in terms of bond distribution model. Electrical properties such as dc conductivity and temperature dependent photoconductivity of investigated thin films were carried out in the temperature range 309-370 K. Analysis of data shows activation energy of dark current is greater as compared to activation energy photocurrent. The value of activation energy decreases with the increase of ion fluence indicates that the defect density of states increases.Also it was found that the value of dc conductivity and photoconductivity increases with the increase of ion fluence.
- OSTI ID:
- 22488837
- Journal Information:
- AIP Conference Proceedings, Vol. 1675, Issue 1; Conference: AMRP-2015: 4. national conference on advanced materials and radiation physics, Longowal (India), 13-14 Mar 2015; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Enhancement of band gap and photoconductivity in gamma indium selenide due to swift heavy ion irradiation
100 MeV Ni{sup +7} swift heavy ion induced magnetism in cobalt doped ZnO thin films
Related Subjects
ABSORPTION SPECTRA
ABSORPTION SPECTROSCOPY
ACTIVATION ENERGY
COMPARATIVE EVALUATIONS
DATA ANALYSIS
DENSITY OF STATES
EVAPORATION
ION BEAMS
IRRADIATION
LITHIUM IONS
PHOTOCONDUCTIVITY
PHYSICAL RADIATION EFFECTS
REFRACTIVE INDEX
SPECTROPHOTOMETRY
SUBSTRATES
TEMPERATURE DEPENDENCE
THIN FILMS
X-RAY DIFFRACTION