The solubility and site preference of Fe{sup 3+} in Li{sub 7−3x}Fe{sub x}La{sub 3}Zr{sub 2}O{sub 12} garnets

Journal Article · Thu Oct 15 00:00:00 EDT 2015 · Journal of Solid State Chemistry

DOI:https://doi.org/10.1016/J.JSSC.2015.01.016· OSTI ID:22486816

Geiger, C. A. ^[1]; Tribus, M.; Tropper, P. ^[2]; Wagner, R.; Tippelt, G.; Lottermoser, W.; Amthauer, G. ^[1]

---

1. Department of Materials Research and Physics, University of Salzburg, 5020 Salzburg (Austria)
2. Institute of Mineralogy and Petrography, Faculty of Geo- and Atmospheric Sciences, University of Innsbruck, Innrain 52, 6020 Innsbruck (Austria)

A series of Fe{sup 3+}-bearing Li{sub 7}La{sub 3}Zr{sub 2}O{sub 12} (LLZO) garnets was synthesized using solid-state synthesis methods. The synthetic products were characterized compositionally using electron microprobe analysis and inductively coupled plasma optical emission spectroscopy (ICP-OES) and structurally using X-ray powder diffraction and {sup 57}Fe Mössbauer spectroscopy. A maximum of about 0.25 Fe{sup 3+} pfu could be incorporated in Li{sub 7−3x}Fe{sub x}La{sub 3}Zr{sub 2}O{sub 12} garnet solid solutions. At Fe{sup 3+} concentrations lower than about 0.16 pfu, both tetragonal and cubic garnets were obtained in the synthesis experiments. X-ray powder diffraction analysis showed only a garnet phase for syntheses with starting materials having intended Fe{sup 3+} contents lower than 0.52 Fe{sup 3+} pfu. Back-scattered electron images made with an electron microprobe also showed no phase other than garnet for these compositions. The lattice parameter, a{sub 0}, for all solid-solution garnets is similar with a value of a{sub 0}≈12.98 Å regardless of the amount of Fe{sup 3+}. {sup 57}Fe Mössbauer spectroscopic measurements indicate the presence of poorly- or nano-crystalline FeLaO{sub 3} in syntheses with Fe{sup 3+} contents greater than 0.16 Fe{sup 3+} pfu. The composition of different phase pure Li{sub 7−3x}Fe{sub x}La{sub 3}Zr{sub 2}O{sub 12} garnets, as determined by electron microprobe (Fe, La, Zr) and ICP-OES (Li) measurements, give Li{sub 6.89}Fe{sub 0.03}La{sub 3.05}Zr{sub 2.01}O{sub 12}, Li{sub 6.66}Fe{sub 0.06}La{sub 3.06}Zr{sub 2.01}O{sub 12}, Li{sub 6.54}Fe{sub 0.12}La{sub 3.01}Zr{sub 1.98}O{sub 12}, and Li{sub 6.19}Fe{sub 0.19}La{sub 3.02}Zr{sub 2.04}O{sub 12}. The {sup 57}Fe Mössbauer spectrum of cubic Li{sub 6.54}Fe{sub 0.12}La{sub 3.01}Zr{sub 1.98}O{sub 12} garnet indicates that most Fe{sup 3+} occurs at the special crystallographic 24d position, which is the standard tetrahedrally coordinated site in garnet. Fe{sup 3+} in smaller amounts occurs at a general 96h site, which is only present for certain Li-oxide garnets, and in Li{sub 6.54}Fe{sub 0.12}La{sub 3.01}Zr{sub 1.98}O{sub 12} this Fe{sup 3+} has a distorted 4-fold coordination. - Graphical abstract: Cubic nominally Li{sub 7}La{sub 3}Zr{sub 2}O{sub 12} (LLZO) garnet is a promising candidate to be used as a solid electrolyte in Li-ion batteries. A series of Fe{sup 3+}-bearing LLZO garnets was synthesized and characterized compositionally and structurally. {sup 57}Mössbauer measurements were made to determine where Fe is incorporated in the crystal structure. X-ray diffraction, electron microprobe, ICP-OES and {sup 57}Mössbauer measurements are needed to obtain a full description of the synthetic products, some of which contain small amounts of nano- or poorly crystalline FeLaO{sub 3}. - Highlights: • A series of Fe{sup 3+}-bearing Li{sub 7}La{sub 3}Zr{sub 2}O{sub 12} (LLZO) garnets was synthesized and characterized compositionally and structurally. • {sup 57}Mössbauer measurements were made to determine where Fe is incorporated in the crystal structure. • Most Fe{sup 3+} substitutes for Li{sup +} in LLZO at the 24d and 96h sites in the cubic phase (Ia-3d). • No more than about 0.25 Fe{sup 3+} pfu can be incorporated into the LLZO garnet structure. • X-ray powder diffractions measurements indicate the presence of both cubic and tetragonal garnets phases in some syntheses. • The probable presence of small amounts of poorly or nano-crystalline FeLaO3 can only be identified by Mössbauer spectroscopy.

• OSTI ID: 22486816
• Journal Information: Journal of Solid State Chemistry, Vol. 230; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
• Country of Publication: United States
• Language: English

Related Subjects

37 INORGANIC
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
CHEMICAL COMPOSITION
CONCENTRATION RATIO
CRYSTAL STRUCTURE
ELECTRON MICROPROBE ANALYSIS
EMISSION SPECTROSCOPY
GARNETS
IONIC CONDUCTIVITY
IRON 57
IRON IONS
LANTHANUM COMPOUNDS
LATTICE PARAMETERS
LITHIUM COMPOUNDS
LITHIUM IONS
NANOSTRUCTURES
SOLID ELECTROLYTES
SOLID SOLUTIONS
SYNTHESIS
X-RAY DIFFRACTION
ZIRCONATES