CTAB-assisted ultrasonic synthesis, characterization and photocatalytic properties of WO{sub 3}

Journal Article · Thu Jan 15 00:00:00 EST 2015 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2014.10.034· OSTI ID:22420754

Gomez-Solis, C.; Torres-Martinez, Leticia M.

Highlights: • WO{sub 3} 2D nanostructures were synthesized by ultrasound method assisted with CTAB. • WO{sub 3} morphology was mainly of rectangular nanoplates with a thickness of ∼50 nm. • The highest surface area value of WO{sub 3} was obtained to lowest concentration of CTAB. • WO{sub 3} activity was attributed to morphology, surface area and the addition of CTAB. • WO{sub 3} nanoplates were able to causing almost complete mineralization of rhB and IC. - Abstract: WO{sub 3} 2D nanostructures have been prepared by ultrasound synthesis method assisted with CTAB using different molar ratios. The formation of monoclinic crystal structure of WO{sub 3} was confirmed by X-ray powder diffraction (XRD). The characterization of the WO{sub 3} samples was complemented by analysis of scanning electron microscopy (SEM), which revealed morphology mainly of rectangular nanoplates with a thickness of around 50 nm and length of 100–500 nm. Infrared spectroscopy (FT-IR) was used to confirm the elimination of the CTAB in the synthesized samples. The specific surface area was determinate by the BET method and by means of diffuse reflectance spectroscopy (DRS) it was determinate the band-gap energy (E{sub g}) of the WO{sub 3} samples. The photocatalytic activity of the WO{sub 3} oxide was evaluated in the degradation reactions of rhodamine B (rhB) and indigo carmine (IC) under Xenon lamp irradiation. The highest photocatalytic activity was observed in the samples containing low concentration of CTAB with morphology of rectangular nanoplates and with higher surface area value than commercial WO{sub 3}. Photodegradation of rhB and IC were followed by means of UV–vis absorption spectra. The mineralization degree of organic dyes by WO{sub 3} photocatalyst was determined by total organic carbon analysis (TOC) reaching percentages of mineralization of 92% for rhB and 50% for IC after 96 h of lamp irradiation.

• OSTI ID: 22420754
• Journal Information: Materials Research Bulletin, Vol. 61; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ABSORPTION SPECTRA
ABSORPTION SPECTROSCOPY
CARBON
CONCENTRATION RATIO
ENERGY GAP
FOURIER TRANSFORMATION
INFRARED SPECTRA
IRRADIATION
MINERALIZATION
MONOCLINIC LATTICES
MORPHOLOGY
NANOSTRUCTURES
PHOTOCATALYSIS
SCANNING ELECTRON MICROSCOPY
SURFACE AREA
SYNTHESIS
TUNGSTEN OXIDES
XENON
X-RAY DIFFRACTION