Electrical properties of samarium cobaltite nanoparticles synthesized using Sol–Gel autocombustion route
Highlights: • The structural evolution and its electrical properties of samarium cobaltite nanograins are discussed. • Optimization of SmCoO{sub 3} nanograins is achieved by post sintering as-prepared gel at 800 °C. • The impedance spectra indicate the semiconducting behavior SmCoO{sub 3} nanograins. - Abstract: Nanograins of SmCoO{sub 3} are prepared by citric acid assisted Sol–Gel autocombustion route. The characterizations of crystal structure, surface morphology and electrical properties of SmCoO{sub 3} powder are done using XRD, HRSEM, FTIR and BDS. The structural evolution of SmCoO{sub 3} upon increasing the annealing temperature is followed using XRD and FTIR analyses. The powder sample contains polycrystalline grains with average size equal to 35 nm and orthorhombic perovskite structure with Pbnm space group. The vibrational bands observed in FTIR spectrum at 545 cm{sup −1} and 439 cm{sup −1} correspond to Co-O stretching modes in cobaltite system. HRSEM images of the sample show the formation of hexagonal shaped grains of samarium cobaltite. The AC electrical conductivity of 4.914 × 10{sup −5} S cm{sup −1} at 295 K is measured for SmCoO{sub 3} nanoparticles. The impedance spectra bring out the semiconducting behavior of the material.
- OSTI ID:
- 22348641
- Journal Information:
- Materials Research Bulletin, Vol. 53; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Synthesis, dielectric behavior and impedance measurement studies of Cr-substituted Zn-Mn ferrites
Synthesis and characterization of novel Ce{sub 0.8}Sm{sub 0.2}Fe{sub 0.9}Ir{sub 0.03}Co{sub 0.07}O{sub 3−δ} perovskite material and possible application as a cathode for low–intermediate temperature SOFCs