Studies on phase formation, microstructure development and elastic properties of reduced NiO-8YSZ anode supported bi-layer half-cell structures of solid oxide fuel cells
- Institute of Northern Engineering, University of Alaska Fairbanks, Fairbanks, AK 99775 (United States)
Highlights: Black-Right-Pointing-Pointer Detailed study on the development of microstructure and phase in NiO-8YSZ anodes. Black-Right-Pointing-Pointer Detailed study on elastic properties at high temperatures in air/reducing atmosphere. Black-Right-Pointing-Pointer Effects of initial porosity, composition and other issues are evaluated in detail. -- Abstract: Half-cell structures of solid oxide fuel cells (SOFCs) with a thin and dense electrolyte layer of 8YSZ supported by a thick and porous NiO-8YSZ anode precursor structure were reduced in a gas mixture of 5% H{sub 2}-95% Ar at 800 Degree-Sign C for selected time periods in order to fabricate cermets with desired microstructure and composition, and to study their effects on the elastic properties at ambient and reactive atmospheres. It appears that 2 h of exposure to the reducing conditions is enough to reduce {approx}80% of NiO with an enhanced porosity value of 35%. The Ni-8YSZ cermet phase formation in the anode was analyzed with X-ray diffraction (XRD) in correlation with its microstructure. The elastic properties were determined after the reduction, at room and elevated temperatures using the impulse excitation technique. At room temperature the decrease in the Young's modulus was about 44% (after 8 h of reduction) and can be attributed mainly to the changes in the microstructure, particularly the increase in porosity from {approx}12% to 37%. Young's moduli of the as-received precursor and reduced anodes were evaluated as a function of temperature in air and reducing atmosphere. The results were explained in correlation to the initial porosity, composition and oxidation of Ni at the elevated temperatures.
- OSTI ID:
- 22212468
- Journal Information:
- Materials Research Bulletin, Vol. 47, Issue 3; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructural changes in NiO–ScSZ composite following reduction processes in pure and diluted hydrogen
Fabrication of hollow mesoporous NiO hexagonal microspheres via hydrothermal process in ionic liquid