Emission Analysis of RE{sup 3+} (= Nd{sup 3+} and Er{sup 3+}) Doped Bi{sub 2}O{sub 3}-B{sub 2}O{sub 3}-LiF Glass Systems
- Department of Physics, Sri Venkateswara University, Tirupati-517 502 (India)
This paper reports on the absorption and emission spectra o of RE{sup 3+} (= Nd{sup 3+} or Er{sup 3+}) doped Bi{sub 2}O{sub 3}-B{sub 2}O{sub 3}-LiF (Bi-B-LiF) glass system. The absorption spectrum of Nd{sup 3+} doped Bi-B-LiF glass has exhibited eight absorption bands at 513 nm, 525 nm, 584 nm, 626 nm, 682 nm, 748 nm, 805 nm and 876 which correspond to the electronic transitions of ({sup 4}I{sub 9/2}{yields}{sup 4}G{sub 9/2}), ({sup 4}I{sub 9/2}{yields}{sup 4}G{sub 9/2}, {sup 4}G{sub 7/2}), ({sup 4}I{sub 9/2}{yields}{sup 4}G{sub 5/2}, {sup 2}G{sub 7/2}), ({sup 4}I{sub 9/2}{yields}{sup 2}H{sub 11/2}), ({sup 4}I{sub 9/2}{yields}{sup 4}F{sub 9/2}), ({sup 4}I{sub 9/2}{yields}{sup 4}F{sub 5/2}, {sup 4}S{sub 3/2}), ({sup 4}I{sub 9/2}{yields}{sup 4}F{sub 5/2}, {sup 2}H{sub 9/2}) and ({sup 4}I{sub 9/2}{yields}{sup 4}F{sub 5/2}) respectively. From Nd{sup 3+} : Bi-B-LiF glass, three NIR emission bands have been observed at 900 nm, 1075 nm and 1342 nm, which are assigned to the transitions of ({sup 4}F{sub 3/2}{yields}{sup 4}I{sub 9/2}), ({sup 4}F{sub 3/2}{yields}{sup 4}I{sub 11/2}) and ({sup 4}F{sub 3/2}{yields}{sup 4}I{sub 13/2}) respectively with an excitation at 514.5 nm (Ar{sup +} ion laser). The Er{sup 3+} : Bi-B-LiF glass has revealed six absorption bands at 489 nm, 522 nm, 653 nm, 800 nm, 973 nm and 1531 nm which are labeled to the transitions of ({sup 4}I{sub 15/2}{yields}{sup 4}F{sub 7/2}), ({sup 4}I{sub 15/2}{yields}{sup 2}H{sub 11/2}, 4G{sub 11/2}), ({sup 4}I{sub 15/2}{yields}{sup 4}F{sub 9/2}), ({sup 4}I{sub 15/2}{yields}{sup 4}I{sub 7/2}), ({sup 4}I{sub 15/2}{yields}{sup 4}I{sub 11/2}), and ({sup 4}I{sub 15/2}{yields}{sup 4}I{sub 13/2}) respectively. From the Er{sup 3+}: Bi-B-LiF glass, an NIR emission at 1540 nm ({sup 4}I{sub 13/2}{yields}{sup 4}I{sub 15/2}), has been observed with an excitation at 514.5 nm (Ar{sup +} ion laser).
- OSTI ID:
- 21608496
- Journal Information:
- AIP Conference Proceedings, Vol. 1372, Issue 1; Conference: NSFD-14: 14. national seminar on ferroelectrics and dielectrics, Bilaspur, Chhattisgarh (India), 2-4 Dec 2010; Other Information: DOI: 10.1063/1.3644455; (c) 2011 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ag{sub 2}O dependent up-conversion luminescence properties in Tm{sup 3+}/Er{sup 3+}/Yb{sup 3+} co-doped oxyfluorogermanate glasses
Visible and infrared luminescence properties of Er{sup 3+}-doped Y{sub 2}Ti{sub 2}O{sub 7} nanocrystals
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
36 MATERIALS SCIENCE
ABSORPTION SPECTRA
ARGON IONS
BISMUTH OXIDES
BORON OXIDES
DIELECTRIC MATERIALS
DOPED MATERIALS
EMISSION SPECTRA
ERBIUM IONS
EXCITATION
FREQUENCY MEASUREMENT
GLASS
LASER RADIATION
LITHIUM FLUORIDES
NEODYMIUM IONS
RHENIUM IONS
ALKALI METAL COMPOUNDS
BISMUTH COMPOUNDS
BORON COMPOUNDS
CHALCOGENIDES
CHARGED PARTICLES
ELECTROMAGNETIC RADIATION
ENERGY-LEVEL TRANSITIONS
FLUORIDES
FLUORINE COMPOUNDS
HALIDES
HALOGEN COMPOUNDS
IONS
LITHIUM COMPOUNDS
LITHIUM HALIDES
MATERIALS
OXIDES
OXYGEN COMPOUNDS
RADIATIONS
SPECTRA