Evidences for decarbonation and exfoliation of layered double hydroxide in N,N-dimethylformamide-ethanol solvent mixture
- Departamento de Quimica Fundamental, Instituto de Quimica, Universidade de Sao Paulo, CP 26077, CEP 05513-900, Sao Paulo, SP (Brazil)
The behavior of a Hydrotalcite-like material (carbonate-containing Mg,Al-layered double hydroxide) in N,N-dimethylformamide (DMF)-ethanol mixture, at ambient temperature, has been investigated. The releasing of CO{sub 2} and production of a formate-containing material occurred mainly for 1:1 (v/v) solvent mixture. Decarbonation of Hydrotalcite is promoted by DMF hydrolysis followed by neutralization of brucite-like layers through HCOO{sup -} intercalation. Translucent colloidal dispersion of LDH nanoparticles from the formate-containing phase was characterized by transmission electron (TEM) and atomic force (AFM) microscopies. The absence of (00l) reflection at X-ray diffraction (XRD) pattern for dried colloidal dispersion indicated delamination of Hydrotalcite. The restacked sample exhibited broad reflections and typical hydroxide ordered layers non-basal (110) diffraction peaks. A LDH-HCOO{sup -} material was also prepared and characterized by FTIR and FT-Raman spectroscopies. Decarbonation and exfoliation of Hydrotalcite in N,N-dimethylformamide-ethanol mixed solvent provide an interesting method for preparation of new intercalated LDH materials. - Graphical abstract: Hydrotalcite suspended in 1:1 (v/v) N,N-dimethylformamide-ethanol solvent mixture, at ambient temperature, undergoes decarbonation and exfoliation. The process is promoted by DMF hydrolysis. Restacking of LDH layers is achieved by evaporating the solvent.
- OSTI ID:
- 21015861
- Journal Information:
- Journal of Solid State Chemistry, Vol. 180, Issue 7; Other Information: DOI: 10.1016/j.jssc.2007.05.003; PII: S0022-4596(07)00192-2; Copyright (c) 2007 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Reversible hydration and aqueous exfoliation of the acetate-intercalated layered double hydroxide of Ni and Al: Observation of an ordered interstratified phase
Structural and morphological characterization of Mg{sub 0.8}Al{sub 0.2}(OH){sub 2}Cl{sub 0.2} hydrotalcite produced by mechanochemistry method
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
AMBIENT TEMPERATURE
AMIDES
ATOMIC FORCE MICROSCOPY
CARBON DIOXIDE
CARBONATES
FORMATES
FOURIER TRANSFORMATION
HYDROLYSIS
HYDROXIDES
INFRARED SPECTRA
LAYERS
MIXED SOLVENTS
NANOSTRUCTURES
PARTICLES
RAMAN SPECTROSCOPY
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION