Charpy Impact Properties of Reduced-Activation Ferritic/Martensitic Steels Irradiated in HFIR up to 20 dpa
- Japan Atomic Energy Research Institute (Japan)
- Oak Ridge National Laboratory (United States)
The effects of irradiation up to 20 dpa on the Charpy impact properties of reduced-activation ferritic/martensitic steels (RAFs) were investigated. The ductile-brittle transition temperature (DBTT) of F82H-IEA shifted up to around 323K. TIG weldments of F82H showed a fairly small variation on their impact properties. A finer prior austenite grain size in F82H-IEA after a different heat treatment resulted in a 20K lower DBTT compared to F82H-IEA after the standard heat treatment, and that effect was maintained even after irradiation. Helium effects were investigated utilizing Ni-doped F82H, but no obvious evidence of helium effects was obtained. ORNL9Cr-2WVTa and JLF-1 steels showed smaller DBTT shifts compared to F82H-IEA.
- OSTI ID:
- 20849514
- Journal Information:
- Fusion Science and Technology, Vol. 44, Issue 1; Other Information: Copyright (c) 2006 American Nuclear Society (ANS), United States, All rights reserved. http://epubs.ans.org/; Country of input: International Atomic Energy Agency (IAEA); ISSN 1536-1055
- Country of Publication:
- United States
- Language:
- English
Similar Records
Neutron irradiation effects on the ductile-brittle transition of ferritic/martensitic steels
Further Charpy impact test results of low activation ferritic alloys, irradiated at 430{degrees}C to 67 dpa