Magnetic properties of Nd-Fe-Ti-C-B nanocomposite magnets produced by spark plasma sintering method
Journal Article
·
· Journal of Applied Physics
- Department of Mechanical Science and Engineering, Chiba Institute of Technology, 2-17-1 Tsudanuma, Narashino, Chiba 275-0016 (Japan)
Amorphous melt-spun ribbons of a Nd{sub 9}Fe{sub 73}Ti{sub 4}C{sub 1}B{sub 13} alloy were consolidated into bulk materials by the spark plasma sintering method. The resultant bulk material was amorphous when the ribbons were consolidated at 773 K. The amorphous bulk material showed a low coercivity, as would be expected for amorphous Nd-Fe-B materials. On the other hand, the bulk materials produced at 873 K and above consisted of {alpha}-Fe and Nd{sub 2}Fe{sub 14}B phases. The resultant nanocomposite magnets showed high coercivity values exceeding 10 kOe. The bulk material produced at 973 K showed a high remanence of 8.4 kG with a maximum energy product of 13.8 MG Oe.
- OSTI ID:
- 20788107
- Journal Information:
- Journal of Applied Physics, Vol. 99, Issue 8; Other Information: DOI: 10.1063/1.2172907; (c) 2006 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Correlation of the energy product with evolution of the nanostructure in Y,Dy,Nd-(Fe,Co)-B magnetic alloy
Correlation of the energy product with evolution of the nanostructure in the Y, Dy, Nd - (Fe, Co) - B magnetic alloy
Structural and magnetic properties of nanocrystalline Fe-rich Fe-Nb-Nd-B sintered magnets produced by consolidating amorphous powders
Journal Article
·
Fri Jul 24 00:00:00 EDT 2009
· J. Appl. Phys.
·
OSTI ID:20788107
+4 more
Correlation of the energy product with evolution of the nanostructure in the Y, Dy, Nd - (Fe, Co) - B magnetic alloy
Journal Article
·
Tue Mar 03 00:00:00 EST 2009
· Journal of Applied Physics
·
OSTI ID:20788107
+4 more
Structural and magnetic properties of nanocrystalline Fe-rich Fe-Nb-Nd-B sintered magnets produced by consolidating amorphous powders
Journal Article
·
Mon Sep 01 00:00:00 EDT 1997
· IEEE Transactions on Magnetics
·
OSTI ID:20788107